LUVOCOM® 1301-8066 VP

Категория PPS, Linear Polyphenylene Sulfide , PPS, Linear
Производитель Lehmann & Voss & Co.
Торговая марка LUVOCOM®
Порт Китай Шанхайский порт
Торговые условия FOB, CFR, CIF
Платежное средство L/C, T/T, Western Union
PDF oi6yMB_LUVOCOM-1301-8066-VP.pdf
Контактная информация
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Описание материалов:
LUVOCOM®1301-8066 VP is a linear polyphenylene sulfide material, and the filler is carbon fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 1301-8066 VP are:
  • Flame Retardant
  • Conductivity
  • High stiffness
  • high strength
  • high viscosity

Typical application areas include:
  • textile/fiber
  • engineering/industrial accessories
  • Automotive Industry
  • business/office supplies
  • medical/health care
Главная Информация
Наполнитель/армирование
  • Армированный материал из углеродного волокна
Добавка
  • Смазка
Характеристики
  • Проводящий
  • Жесткий, высокий
  • Высокая прочность
  • Защита от электростатического разряда
  • Хорошее сопротивление ползучести
  • Теплостойкость, высокая
  • Смазка
  • Вязкость, высокая
  • Огнестойкий
Используется
  • Текстильные изделия
  • Инженерные аксессуары
  • Применение в автомобильной области
  • Бизнес-оборудование
  • Медицинские принадлежности/принадлежности для ухода
Внешний вид
  • Темно-серый
ФизическийНоминальное значениеЕдиница измеренияМетод испытания
Плотность 1.56g/cm³ISO 1183
Формовочная усадка 0.050 - 0.30%DIN 16901
Поглощение воды (23°C, 24 hr)< 0.050%
МеханическиеНоминальное значениеЕдиница измеренияМетод испытания
Модуль растяжения 21000MPaISO 527-2
Tensile Stress (Break)170MPaISO 527-2
Растяжимое напряжение (Yield)1.3%ISO 527-2
Флекторный модуль 18000MPaISO 178
Флекторный стресс 240MPaISO 178
Flexural Strain at Flexural Strength 1.6%ISO 178
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Максимальная рабочая температура- Короткий срок 240°C
ЭлектрическийНоминальное значениеЕдиница измеренияМетод испытания
Insulation Resistance ohmsIEC 60167
ВоздействиеНоминальное значениеЕдиница измеренияМетод испытания
Charpy Unnotched Impact Strength (23°C)35kJ/m²ISO 179/1eU
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Температура непрерывного использования 220°CUL 746B
ЭлектрическийНоминальное значениеЕдиница измеренияМетод испытания
Удельное сопротивление поверхности < 1.0E+3ohmsIEC 60093
ИнъекцияНоминальное значениеЕдиница измерения
Температура сушки
    B 50.0 - 90.0°C
    Hot air dryer, A 100 - 140°C
Время сушки
    B > 4.0hr
    Hot air dryer, A 2.0 - 4.0hr
Задняя температура 300 - 320°C
Средняя температура 310 - 330°C
Передняя температура 320 - 340°C
Температура сопла 320 - 340°C
Температура обработки (расплава) 330°C
Температура формы 150 - 180°C
Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information The material does not necessarily have to be predried; when originally sealed containers are used, this process may normally be omitted. Processing temperatures above 360°C may very rapidly cause thermal damage and should therefore be avoided. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.
Тип материала Категория Производитель
Infino XP-2150IM PPS SAMSUNG SDI CO., LTD.
LNP™ THERMOCOMP™ 9X11428J compound PPS SABIC Innovative Plastics
Quadrant EPP BG PPS PPS Quadrant Engineering Plastic Products
Fortron® 1140L7 PPS Celanese Corporation
Star L PPS D93F PPS Eurostar Engineering Plastics
Polygen SFG6C-BK PPS Shanghai Polygen Science and Technology Co., Ltd.
Получите информацию об этом продукте следующим способом.
Телефон+086 13424755533
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Copyright © russianpolymer.com All Rights Reserved
Получите информацию об этом продукте следующим способом.
+08613424755533
sales@su-jiao.com

Служба поддержки клиентов Вичат
Свяжитесь с нами