Описание материалов:
TN2020 is an Ethylene-Vinyl Acetate (EVA) copolymer, developed to mostly meet the needs of the multi-layer packaging segment produced by coextrusion and/or lamination processes. Multilayer structures with TN2020 can be irradiated to improve physical proprieties, such as, adhesion between layers, puncture resistance and hot sealing. Since it presents an exceptional weldability, this product meets the requirements for automatic or semi-automatic lines of cutting, welding, and/or packaging (with or without vacuum-packed process). It has excellent performance during the extrusion operation, thermal stability, and a low consumption of energy for its processing, rendering to package production a dimensional uniformity and excellent visual properties with high transparency and gloss that enhance the printing and surface finish of the packaging.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Антиоксидант
- Сополимер
- Отличная Печатающая способность
- Хорошая поверхность
- Хорошая термическая стабильность
- Высокая четкость
- Глянцевый
- Свариваемый
|
| Используется | - Пленка
- Пищевая упаковка
- Упаковка
- Термоусадочная пленка
|
| Рейтинг агентства | - Управление по санитарному надзору за качеством пищевых продуктов и медикаментов 21 CFR 177,1350
|
| Метод обработки | - Соэкструдированная пленка
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.931 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Содержание винилацетата | 8.5 | wt% | |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра | | | ASTM D2240 |
| Shore A, Compression Molded | 93 | | |
| Shore D, Compression Molded | 45 | | |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение (Break, Compression Molded) | 19.0 | MPa | ASTM D638 |
| Удлинение при растяжении (Break, Compression Molded) | 700 | % | ASTM D638 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 50 | µm | |
| Сектантный модуль | | | ASTM D882 |
| 2% Secant, MD
: 50 µm, Blown Film | 76.0 | MPa | |
| 2% Secant, TD
: 50 µm, Blown Film | 79.0 | MPa | |
| Прочность на растяжение | | | ASTM D882 |
| MD
: Break, 50 µm, Blown Film | 24.0 | MPa | |
| TD
: Break, 50 µm, Blown Film | 20.0 | MPa | |
| Удлинение при растяжении | | | ASTM D882 |
| MD
: Break, 50 µm, Blown Film | 440 | % | |
| TD
: Break, 50 µm, Blown Film | 750 | % | |
| Ударное падение Dart (50 µm, Blown Film) | 230 | g | ASTM D1709B |
| Elmendorf Tear Strength | | | ASTM D1922 |
| MD
: 50 µm, Blown Film | 330 | g | |
| TD
: 50 µm, Blown Film | 250 | g | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Викат Температура размягчения | 79.0 | °C | ASTM D1525 1 |
| Пиковая температура плавления | 100 | °C | ASTM D3418 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блеск (45°, 50.0 µm, Blown Film) | 86 | | ASTM D2457 |
| Haze (50.0 µm, Blown Film) | 1.8 | % | ASTM D1003 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | 135 to 185 | °C | |
| Примечание |
|---|
| 1 . | Loading 1 (10 N) |