Andur 8003 AS/Ethacure® 100LC
Описание материалов:
Andur 8003AS is a 80 Shore A, low cost, high performance urethane. Andur 8003AS offers high rebound and excellent dynamic properties in a moderate to low cost system. In addition, when properly cast, Andur 8003AS gives a water white finished product. Andur 8003AS performs best when cast with Ethacure 100LC through meter mix and dispense equipment however, product modifications are available which may extend working time to offer hand batch opportunities. This system is primarily recommended for applications that require superior dynamic performance, or enhanced product clarity. In addition, low processing temperatures and quick cycle times offer processing advantages.
| Главная Информация | |
|---|
| Характеристики | - Обрабатываемость, хорошая
- Цикл быстрого формования
- Высокое разрешение
|
| Формы | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 1.07 | g/cm³ | ASTM D1505 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore A) | 81 | | ASTM D2240 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ASTM D412 |
| 100% strain | 3.45 | MPa | ASTM D412 |
| 300% strain | 6.21 | MPa | ASTM D412 |
| Прочность на растяжение (Yield) | 23.4 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 850 | % | ASTM D412 |
| Сопротивляемость Bayshore | 60 | % | ASTM D2632 |
| Термокомплект | Номинальное значение | Единица измерения | |
|---|
| Срок службы горшка | 1.8 | min | |
| Время демолд (100°C) | 15 | min | |
| Время доставки (100°C) | 16 | hr | |
| Дополнительная информация |
|---|
| Durometer Hardness, ASTM D2240, Shore A: 80 to 82Die C Tear, ASTM D1004: 330 pliAverage Split Tear, ASTM D1938: 135 pliStoichiometry Curative Level: 95%Mix Temperature:
Andur 8003 AS: 75°F
Ethacure 100LC: 75°F |