Описание материалов:
Cling MB
Description
POOYATAK CG203 is a PE based master batch containing a tackifying resin is used as a cling agent. It can be used in LLDPE or LDPE based stretch wrap and cling wrap films for pallet wrapping, silage wrapping and food packaging whether by blown or cast processing. The agent migrates to the film surface within 24 to 72 hours and exhibits the cling properties by then.
There must neither be any slip or antiblock agent in the film base resin nor as masterbatch in the formulas.
Application
POOYATAK CG203 is designed for ease of dilution and homogeneous mixing and is therefore suitable for direct addition using automatic dosing units or by pre-blending. Depending on the film thickness (the thicker film needs less addition level), process (the blown process needs double dosage), film cooling temperature (higher cooling temperature needs more level) and the final application it can be used from 2 to 10%.
It should be stored in a dry and cool place not to exceed 6 month.
Description
POOYATAK CG203 is a PE based master batch containing a tackifying resin is used as a cling agent. It can be used in LLDPE or LDPE based stretch wrap and cling wrap films for pallet wrapping, silage wrapping and food packaging whether by blown or cast processing. The agent migrates to the film surface within 24 to 72 hours and exhibits the cling properties by then.
There must neither be any slip or antiblock agent in the film base resin nor as masterbatch in the formulas.
Application
POOYATAK CG203 is designed for ease of dilution and homogeneous mixing and is therefore suitable for direct addition using automatic dosing units or by pre-blending. Depending on the film thickness (the thicker film needs less addition level), process (the blown process needs double dosage), film cooling temperature (higher cooling temperature needs more level) and the final application it can be used from 2 to 10%.
It should be stored in a dry and cool place not to exceed 6 month.
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Внешний вид |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.910 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (120°C/1.2 kg) | 5.0 to 11 | g/10 min | ASTM D1238 |
| Moisture Content | < 2000 | ppm | ASTM D644 |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Pellet Size | 40.0 to 50.0 | pcs/cm³ | Internal Method |
| Тип материала | Категория | Производитель |
|---|---|---|
| LITEN MB 73 | PE Homopolymer | UNIPETROL RPA |
| REVOLVE® M-762 | PE, Unspecified | Matrix Polymers |
| Spherisil P 23-08660 | PE, Unspecified | SILON s.ro |
| Hyundai EP Adhesives MP300JA/7900 | PE, Unspecified | HYUNDAI EP Co., Ltd. |
| Teslin® SP 800 | PE, Unspecified | PPG Industries, Inc. |
| Matrixx FPE3A20CC | PE, Unspecified | The Matrixx Group, Inc. |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved