DOW™ Electrical & Telecommunications HFDA-5630 BK

Категория PE, Crosslinkable Power Cable Insulation Compound , PE Copolymer
Производитель The Dow Chemical Company
Торговая марка DOW™ Electrical & Telecommunications
Порт Китай Шанхайский порт
Торговые условия FOB, CFR, CIF
Платежное средство L/C, T/T, Western Union
PDF nqlvTP_DOW-Electrical-Telecommunications-HFDA-5630-BK.pdf
Контактная информация
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Описание материалов:
Power cable insulation material

HFDA-5630 Black is a curable polyethylene copolymer with a medium addition of carbon black by thermal cracking method, which is used as a wire insulation material. It is recommended to apply to 600volt power cables and control cables.

Specifications
HFDA-5630 Black has been UL certified and can be used in XHHW, XHHW-2, RHH, RHW, RHW-2, SIS,USE and USE-2 applications.

When adopting the correct commercial manufacturing specifications, cables using HFDA-5630 Black should meet the following industry cable specifications:
  • ICEA: S-66-524; NEMA WC7
Главная Информация
Наполнитель/армирование
  • Армированный материал из углеродного волокна
Используется
  • Изоляция низкого напряжения
  • Применение проводов и кабелей
  • Промышленный изоляционный материал кабеля
Формы
  • Частицы
ФизическийНоминальное значениеЕдиница измеренияМетод испытания
Удельный вес 1.07g/cm³ASTM D792
ТвердостьНоминальное значениеЕдиница измеренияМетод испытания
Твердость дюрометра (Shore D)48ASTM D2240
МеханическиеНоминальное значениеЕдиница измеренияМетод испытания
Модуль растяжения- Сектант 80.7MPaASTM D638
ЭластомерыНоминальное значениеЕдиница измеренияМетод испытания
Прочность на растяжение (Break)17.9MPaASTM D412
Удлинение при растяжении (Break)430%ASTM D412
СтарениеНоминальное значениеЕдиница измеренияМетод испытания
Прочность на растяжение- 14 дней (150°C)100%ASTM D412
Удлинение- 14 дней (150°C)87%ASTM D412
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Температура ломкости 1-80.0°CASTM D746
ЭлектрическийНоминальное значениеЕдиница измеренияМетод испытания
Сопротивление громкости (23°C)1.0E+14ohms·cmASTM D257
Диэлектрическая прочность ASTM D149
    3.18 mm 215kV/mmASTM D149
    3.18 mm 314kV/mmASTM D149
Диэлектрическая постоянная (60 Hz)5.00ASTM D150
Коэффициент рассеивания (60 Hz)6.0E-3ASTM D150
Дополнительная информация
Nominal property values above represent tests on molded stress-relieved slabs. Cure times were 15 minutes at 175°C.
ЭкструзияНоминальное значениеЕдиница измерения
Температура бункера 65.6°C
Температура расплава 116 - 135°C
Инструкции по экструзии
HFDA-5630 BK provides excellent surface finish and outstanding output rates over a broad range of conditions. For optimum results, use melt extrusion temperatures in the suggested range of 240-275°F (115-135°C). However, specific recommendations for processing conditions can be determined only when the application and type of processing equipment are known. Please contact your local Dow Wire and Cable sales representative for such particulars. Hopper drying at 150°F (65°C) before extrusion is recommended to remove moisture.
Примечание
1 .F20
2 .Method A (short time)
3 .Method B (step by step)
Тип материала Категория Производитель
POOYATAK CG203 PE, Unspecified Pooya Polymer Tehran
Favorite A190 PE, Unspecified Favorite Plastics
Fusabond® E528 PE, Unspecified DuPont Packaging & Industrial Polymers
ICORENE® 9031 BA8 PE, Unspecified ICO Polymers SA, A Division of A. Schulman
GAPEX® RPE40HW11NA PE, Unspecified Ferro Corporation
Teslin® SPID 1000 PE, Unspecified PPG Industries, Inc.
Получите информацию об этом продукте следующим способом.
Телефон+086 13424755533
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат