PolyFR® 200 is a highly loaded non-halogen flame retardant concentrate pellet designed for ease of use in polypropylene product compounding and molding processes where FR levels can be metered in to meet various flame retardant standards for the product. The concentrate incorporates our high performance JJAZZ® intumescent flame retardant system. PolyFR® 200 utilizes a prime 20 melt polypropylene as its binder resin to provide good balance of properties when blended with a variety of other polypropylene resins in final compounding and molding applications. It is recommended at loading levels from 35-50% depending on the resin systems, material thickness, equipment, formulation additives and final flame retardancy requirements. It is recyclable.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Огнестойкий
- Без галогенов
- Низкий до без дыма
- Не Цветущий
- Перерабатываемый материал
|
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.18 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (230°C/2.16 kg) | 0.49 | g/10 min | ASTM D1238 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура ломкости | -52.8 | °C | ASTM D746 |
| Воспламеняемость | Номинальное значение | | Метод испытания |
|---|
| Огнестойкость (1.59 mm, 40% loading) | V-0 | | UL 94 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 105 | °C | |
| Время сушки | 2.0 to 4.0 | hr | |
| Температура обработки (расплава) | 185 to 195 | °C | |