Westlake LLDPE LF2020
| Категория | LLDPE, Linear Low Density Polyethylene |
| Производитель | Westlake Chemical Corporation |
| Торговая марка | Westlake LLDPE |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
nEzYhk_Westlake-LLDPE-LF2020.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Westlake LF2020 is a hexene LLDPE with excellent physical properties and heat sealing characteristics, which allow for down-gauging and blending with other materials. Typical applications include stretch films, heavy duty bags and sacks, agricultural films, and trash bags & liners. This material is a available with various slip and antiblock levels.
Application/Uses:
Bags and sacks
Agricultural films
Trash bags and line
Co-extruded structures
Application/Uses:
Bags and sacks
Agricultural films
Trash bags and line
Co-extruded structures
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.919 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 25 | µm | |
| Сектантный модуль 1 | ASTM D882 | ||
| 1% secant, MD : 25 µm, blown film | 207 | MPa | ASTM D882 |
| 1% secant, TD : 25 µm, blown film | 248 | MPa | ASTM D882 |
| Прочность на растяжение 2 | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 40.7 | MPa | ASTM D882 |
| TD : Broken, 25 µm, blown film | 28.3 | MPa | ASTM D882 |
| Удлинение при растяжении 3 | ASTM D882 | ||
| MD : Broken, 25 µm, blown film | 670 | % | ASTM D882 |
| TD : Broken, 25 µm, blown film | 900 | % | ASTM D882 |
| Ударное падение Dart 4(25 µm, Blown Film) | 220 | g | ASTM D1709A |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Haze (25.4 µm, Blown Film) | 15 | % | ASTM D1003 |
| Дополнительная информация |
|---|
| Test specimens for blown film: nominal thickness 1.0 mils fabricated at 2.5:1 BUR. |
| Экструзия | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Температура расплава | 204 - 216 | °C |
| Примечание | |
|---|---|
| 1 . | Test run at 23°C (73°F) and 50% relative humidity |
| 2 . | Test run at 23°C (73°F) and 50% relative humidity |
| 3 . | Test run at 23°C (73°F) and 50% relative humidity |
| 4 . | F50 |
| Тип материала | Категория | Производитель |
|---|---|---|
| MORETEC™ 0248CN | LLDPE | Prime Polymer Co., Ltd. |
| Bapolene® 222F | LLDPE | Bamberger Polymers, Inc. |
| Braskem PE SLL218/21 | LLDPE | Braskem |
| HANWHA CHBA-8806FR | LLDPE | Hanwha Chemical |
| ICORENE® 3560 | LLDPE | ICO Polymers NA, A Division of A. Schulman |
| Plexar® PX5335 | LLDPE | LyondellBasell Industries |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved