Описание материалов:
Durastar™ DS2000 polymer has excellent appearance and is nearly water-clear. Its most outstanding features are toughness, chemical resistance, and excellent processing characteristics. DS2000 has very good toughness as shown by Izod impact resistance. Exposure to aromatic oils often causes crazing or actual fracture of many polymer resins, but DS2000 maintains its physical properties when exposed to these oils, and its appearance is virtually unchanged. Easy to process, it flows readily and fills intricate molds. Under existing United States Food and Drug Administration (FDA) regulations, Durastar™ DS2000 may be used in food contact articles which comply with the specifications and conditions of use in 21 CFR 177.1240.
| Главная Информация | |
|---|
| Характеристики | - Цикл быстрого формования
- Приемлемый пищевой контакт
- Хорошая химическая стойкость
- Хороший поток
- Хорошая ударопрочность
- Хорошая технологичность
- Хорошая прочность
- Высокая четкость
- Приятный внешний вид
|
| Используется | - Спортивные товары
- Игрушки
- Инструменты для письма
|
| Рейтинг агентства | - Управление по санитарному надзору за качеством пищевых продуктов и медикаментов 21 CFR 177,1240
|
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | | | |
| -- | 1.20 | g/cm³ | ASTM D792 |
| 23°C | 1.19 | g/cm³ | ISO 1183 |
| Формовочная усадка-
Поток (3.20 mm) | 0.20 to 0.60 | % | ASTM D955 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale, 23°C) | 105 | | ASTM D785 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение | | | |
| Yield, 23°C | 46.0 | MPa | ASTM D638 |
| Yield, 23°C | 47.0 | MPa | ISO 527-2 |
| Break, 23°C | 53.0 | MPa | ASTM D638 |
| Break, 23°C | 49.0 | MPa | ISO 527-2 |
| Удлинение при растяжении | | | |
| Yield, 23°C | 5.0 | % | ASTM D638 |
| Yield, 23°C | 4.0 | % | ISO 527-2 |
| Break, 23°C | 310 | % | ASTM D638 |
| Break, 23°C | 210 | % | ISO 527-2 |
| Флекторный модуль | | | |
| 23°C | 1900 | MPa | ASTM D790 |
| 23°C | 1750 | MPa | ISO 178 |
| Флекторный стресс | | | |
| 23°C | 64.0 | MPa | ISO 178 |
| Yield, 23°C | 67.0 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | | | |
| -40°C | 60 | J/m | ASTM D256 |
| 23°C | 370 | J/m | ASTM D256 |
| -40°C | 6.3 | kJ/m² | ISO 180 |
| 23°C | 30 | kJ/m² | ISO 180 |
| Незубчатый изод Impact | | | ASTM D4812 |
| -40°C | No Break | | |
| 23°C | No Break | | |
| Ударное устройство для дротиков | | | |
| -40°C, Energy at Peak Load | 48.0 | J | ASTM D3763 |
| 23°C, Energy at Peak Load | 45.0 | J | ASTM D3763 |
| -40°C, Energy to Peak Force | 55.0 | J | ISO 6603-2 |
| 23°C, Energy to Peak Force | 71.0 | J | ISO 6603-2 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | |
| 0.45 MPa, Unannealed | 73.0 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 66.0 | °C | ISO 75-2/A |
| Воспламеняемость | Номинальное значение | | Метод испытания |
|---|
| Огнестойкость (1.50 mm, CL) | HB | | UL 94 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Коэффициент пропускания | | | ASTM D1003 |
| Total | 91.0 | % | |
| Regular | 89.0 | % | |
| Haze | 0.30 | % | ASTM D1003 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 70.0 | °C | |
| Время сушки | 3.0 | hr | |
| Температура обработки (расплава) | 250 to 290 | °C | |
| Температура формы | 15.0 to 30.0 | °C | |