Andur M-22 (97% HQEE/ 3%TMP)
Описание материалов:
Andur M-22 is an MDI-Ester prepolymer that, when processed with close attention to handling procedures and formulation, produces high quality elastomers. These elastomers perform very well in dynamic applications.
| Твердость | Номинальное значение | | Метод испытания |
|---|
| Твердость дюрометра | | | ASTM D2240 |
| Shaw A | 94 | | ASTM D2240 |
| Shaw D | 45 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на сжатие | | | ASTM D695 |
| 2% strain | 0.965 | MPa | ASTM D695 |
| 5% strain | 1.90 | MPa | ASTM D695 |
| 10% strain | 3.10 | MPa | ASTM D695 |
| 15% strain | 3.72 | MPa | ASTM D695 |
| 20% strain | 5.17 | MPa | ASTM D695 |
| 25% strain | 6.55 | MPa | ASTM D695 |
| 50% strain | 18.6 | MPa | ASTM D695 |
| Устойчивость к истиранию | 42.0 | mg | ASTM D1044 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ASTM D412 |
| 100% strain | 7.58 | MPa | ASTM D412 |
| 300% strain | 14.5 | MPa | ASTM D412 |
| Прочность на растяжение (Yield) | 41.4 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 600 | % | ASTM D412 |
| Комплект сжатия | 34 | % | ASTM D395 |
| Термокомплект | Номинальное значение | Единица измерения | |
|---|
| Срок службы горшка | 6.0 - 10 | min | |
| Время демолд | 90 | min | |
| Дополнительная информация |
|---|
| Die C Tear, ASTM D1004: 805 pliAverage Split Tear, ASTM D1938: 320 pliStoichiometry Curative Level: 90%Break Set, ASTM D412-80: 30%NBS Abrasion: 250% Rubber StandardParts of curative per 100 parts Andur M-22, 6.5% NCO: 13.7 parts by weightParts of curative per 100 parts Andur M-22, 6.55% NCO: 13.8 parts by weightParts of curative per 100 parts Andur M-22, 6.6% NCO: 13.91 parts by weightParts of curative per 100 parts Andur M-22, 6.65% NCO: 14.01 parts by weightParts of curative per 100 parts Andur M-22, 6.7% NCO: 14.12 parts by weightMix Temperature:
Andur M-22: 221-230°F
Curative HQEE/TMP: 230°F
Stability:
Ambient Temperature, 25°C: 6 Months
Melting Temperature, 60°C: 1 Month
Processing Temperature, 90°C: 12 Hours
Processing Temperature, 105°C: 3 Hours |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 110 - 140 | °C | |