Описание материалов:
LUVOCOM®1/GF/20/TF/10/SI/2/NC is a polyamide 66 (nylon 66) material, which contains a 20% glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 1/GF/20/TF/10/SI/2/NC are:
  • flame retardant/rated flame
  • Lubrication
  • Good stiffness
  • Wear-resistant

Typical application areas include:
  • engineering/industrial accessories
  • Electrical/electronic applications
  • textile/fiber
  • Automotive Industry
  • business/office supplies
Главная Информация
Наполнитель/армирование
  • Армированный стекловолокном материал, 20% наполнитель по весу
Добавка
  • PTFE лубрикант (10%)
  • Силиконовая смазка (2)
Характеристики
  • Низкий коэффициент трения
  • Жесткий, хороший
  • Хорошая прочность
  • Хорошая стойкость к истиранию
  • Смазка
Используется
  • Шестерня
  • Текстильные изделия
  • Инженерные аксессуары
  • Переключатель
  • Применение в автомобильной области
  • Бизнес-оборудование
  • Подшипник
Внешний вид
  • Натуральный цвет
ФизическийНоминальное значениеЕдиница измеренияМетод испытания
Плотность 1.36g/cm³ISO 1183
Формовочная усадка 0.30 - 0.60%DIN 16901
Поглощение воды (23°C, 24 hr)< 1.0%
МеханическиеНоминальное значениеЕдиница измеренияМетод испытания
Модуль растяжения 7000MPaISO 527-2
Tensile Stress (Break)150MPaISO 527-2
Растяжимое напряжение (Yield)3.0%ISO 527-2
Флекторный модуль 6500MPaISO 178
Флекторный стресс 225MPaISO 178
Коэффициент трения
    Dynamic 0.13
    Static 0.11
Flexural Strain at Flexural Strength 4.0%ISO 178
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Максимальная рабочая температура- Короткий срок 150°C
ЭлектрическийНоминальное значениеЕдиница измеренияМетод испытания
Insulation Resistance > 1.0E+12ohmsIEC 60167
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Температура непрерывного использования 90.0°CUL 746B
Викат Температура размягчения 250°CISO 306/A
ЭлектрическийНоминальное значениеЕдиница измеренияМетод испытания
Удельное сопротивление поверхности > 1.0E+12ohmsIEC 60093
ВоспламеняемостьНоминальное значениеЕдиница измеренияМетод испытания
Огнестойкость HBUL 94
ИнъекцияНоминальное значениеЕдиница измерения
Температура сушки
    Hot air dryer, A 75.0°C
    Vacuum dryer, B 105°C
Время сушки
    Hot air dryer, A 6.0 - 16hr
    Vacuum dryer, B 4.0 - 6.0hr
Рекомендуемая максимальная влажность 0.10%
Задняя температура 290 - 310°C
Средняя температура 290 - 310°C
Передняя температура 290 - 310°C
Температура сопла 280 - 300°C
Температура обработки (расплава) 290°C
Температура формы 90.0 - 120°C
Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. Due to rapid absorption of water, originally sealed containers should only be opened immediately prior to processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.
Тип материала Категория Производитель
Nylene® 4114-14 GL Nylon 66 Custom Resins Group
EMLON® 66 GFR 35 Nylon 66 EMAS Plastik San.Tic.AS.
KOPA® KN3322V0 Nylon 66 Kolon Plastics, Inc.
KOPLA PA66 KDG1050 Nylon 66 KOPLA Co., Ltd.
4TECH® 9A22710 H Nylon 66 4Plas
BESTNYL SE15VI02AS16 Nylon 66 Triesa Plastics
Получите информацию об этом продукте следующим способом.
Телефон+086 13424755533
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Copyright © russianpolymer.com All Rights Reserved
Получите информацию об этом продукте следующим способом.
+08613424755533
sales@su-jiao.com

Служба поддержки клиентов Вичат
Свяжитесь с нами