Описание материалов:
DOWLEX™2042E polyethylene resin is an ethylene/1-octene copolymer, which is suitable for the production and processing of blown films. These blown films require good tear strength, excellent toughness, good stiffness and high temperature resistance.
Remarks: When used in the application field of contact with food, DOWLEX 2042E polyethylene resin should comply with the U.S. Food and Drug Administration regulations when it is unmodified and the processing process follows the requirements of good manufacturing practices. The requirements of the 177.1520, the Canadian Health Products and Food Agency (HPFB) -no objection (with restrictions) and the requirements of the food contact regulations of most European countries.
Please contact your nearest Dow representative for proof of compliance with the food contact law. The purchaser remains responsible for determining whether the use of its products complies with all relevant regulations.
| Главная Информация | |
|---|
| Рейтинг агентства | - Управление по санитарному надзору за качеством пищевых продуктов и медикаментов 21 CFR 177,1520
- HPFB (Канада) без возражения 2
|
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес 1 | 0.930 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore D, Compression Molded) | 57 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения-
2% Secant (Compression Molded) | 340 | MPa | ASTM D638 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 25 | µm | |
| Энергия прокола пленки (25 µm) | 1.00 | J | Internal method |
| Прочность на растяжение | | | ASTM D882 |
| MD
: Yield, 25 µm | 14.0 | MPa | ASTM D882 |
| TD
: Yield, 25 µm | 17.0 | MPa | ASTM D882 |
| MD
: Break, 25 µm | 42.0 | MPa | ASTM D882 |
| TD
: Break, 25 µm | 41.0 | MPa | ASTM D882 |
| Удлинение при растяжении | | | ASTM D882 |
| MD
: Break, 25 µm | 830 | % | ASTM D882 |
| TD
: Break, 25 µm | 1100 | % | ASTM D882 |
| Ударное падение Dart (25 µm) | 90 | g | ASTM D1709 |
| Elmendorf Tear Strength | | | ASTM D1922 |
| MD
: 25 µm | 100 | g | ASTM D1922 |
| TD
: 25 µm | 620 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Викат Температура размягчения 2 | 118 | °C | ASTM D1525 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блеск (20°, 25.0 µm) | 30 | | ASTM D2457 |
| Haze (25.0 µm) | 12 | % | ASTM D1003 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | 190 - 240 | °C | |
| Инструкции по экструзии |
|---|
| 管形薄膜挤出的制造条件：
熔体温度：190 至 240°C。
放大比范围：1.5 至 3:1
建议的厚度范围：10 至 150 µm。 |
| Примечание |
|---|
| 1 . | Compression molding |
| 2 . | Compression molding |