Описание материалов:
Duratron® U2300 is an extruded 30% glass reinforced polyetherimide. It is an amorphous, high-performance polymer with exceptional flame and heat resistance. It performs continuously to 340°F (171°C), making it ideal for high strength/high heat applications, and those requiring consistent dielectric properties over a wide frequency range. It is hydrolysis resistant, highly resistant to acidic solutions and capable of withstanding multiple autoclaving cycles.
Duratron® U2300 provides greater rigidity and improved dimensional stability while maintaining many of the useful characteristics of unfilled Duratron® PEI. Duratron® PEI commonly is machined into parts for reusable medical devices, analytical instrumentation, electrical/electronic insulators and a variety of structural components requiring high strength and rigidity at elevated temperatures.
Data provided by Quadrant Engineering Plastic Products from tests on stock shapes and parts produced by Quadrant EPP.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Стекловолокно, 30% наполнитель по весу
|
| Характеристики | - Кислотоупорный
- Устойчивость к воздействию алкоголя
- Аморфный
- Автоклавный
- Огнестойкий
- Хорошая стабильность размеров
- Высокая термостойкость
- Высокая жесткость
- Высокая прочность
- Устойчивость к гидролизу
|
| Используется | - Электрическое/электронное применение
- Изоляция
- Медицинские/медицинские приложения
- Детали конструкции
|
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.51 | g/cm³ | ASTM D792 |
| Поглощение воды | | | ASTM D570 |
| 24 hr | 0.18 | % | |
| Saturation | 0.90 | % | |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла | | | ASTM D785 |
| M-Scale | 114 | | |
| R-Scale | 127 | | |
| Твердость дюрометра (Shore D) | 86 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 5520 | MPa | ASTM D638 |
| Прочность на растяжение (Ultimate) | 117 | MPa | ASTM D638 |
| Удлинение при растяжении (Break) | 3.0 | % | ASTM D638 |
| Флекторный модуль | 5860 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 186 | MPa | ASTM D790 |
| Компрессионный модуль | 4310 | MPa | ASTM D695 |
| Прочность на сжатие (10% Strain) | 221 | MPa | ASTM D695 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | 53 | J/m | ASTM D256A |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке (1.8 MPa, Unannealed) | 210 | °C | ASTM D648 |
| Максимальная температура использования-
Долгосрочный, воздушный | 171 | °C | |
| Температура перехода стекла | 210 | °C | ASTM D3418 |
| CLTE-
Поток 1(-40 to 149°C) | 2.0E-5 | cm/cm/°C | ASTM E831 |
| Теплопроводность | 0.23 | W/m/K | ASTM F433 |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельное сопротивление поверхности 2 | > 1.0E+13 | ohms | Internal Method |
| Диэлектрическая прочность 3 | 30 | kV/mm | ASTM D149 |
| Диэлектрическая постоянная (1 MHz) | 3.70 | | ASTM D150 |
| Коэффициент рассеивания (1 MHz) | 1.5E-3 | | ASTM D150 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость (3.18 mm, Estimated Rating) | V-0 | | UL 94 |
| Примечание |
|---|
| 1 . | 68°F |
| 2 . | EOS/ESD S11.11 |
| 3 . | Method A (Short-Time) |