Описание материалов:
Baytec MS-051 is a modified diphenylmethane diisocyanate (MDI)-terminated polyester prepolymer used in the manufacture of high-property solid cast polyurethane elastomers. The excellent resilience and low compression-set properties have enabled this material to be used for low-durometer wheels, printing rolls, and squeegee blades. As with any product, use of Baytec MS-051 prepolymer in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Характеристики | - Низкая деформация сжатия
- Гибкий
|
| Используется | |
| Формы | |
| Твердость | Номинальное значение | | Метод испытания |
|---|
| Твердость дюрометра (Shore A) | 80 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Устойчивость к истиранию (1000 Cycles, 1000 g, H-18 Wheel) | 16.0 | mg | ASTM D4066 |
| Отклонение сжатия | | | ASTM D575 |
| 10% | 1.52 | MPa | ASTM D575 |
| 15% | 2.28 | MPa | ASTM D575 |
| 2% | 0.241 | MPa | ASTM D575 |
| 20% | 3.07 | MPa | ASTM D575 |
| 25% | 3.93 | MPa | ASTM D575 |
| 5% | 0.724 | MPa | ASTM D575 |
| 50% | 10.9 | MPa | ASTM D575 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ASTM D412 |
| 100% strain | 4.41 | MPa | ASTM D412 |
| 200% strain | 6.00 | MPa | ASTM D412 |
| 300% strain | 8.14 | MPa | ASTM D412 |
| Прочность на растяжение (Break) | 37.0 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 530 | % | ASTM D412 |
| Tear Strength | | | |
| -- 1 | 66.5 | kN/m | ASTM D624 |
| Cracking | 18 | kN/m | ASTM D1938 |
| Комплект сжатия (70°C, 22 hr) | 24 | % | ASTM D395 |
| Сопротивляемость Bayshore | 52 | % | ASTM D2632 |
| Дополнительная информация |
|---|
| Appearance: Light amber liquidNCO: 4.9 to 5.2 wt%Flash Point, PMCC: >93°CSpecific Gravity at 80°C: 1.18Specific Gravity at 100°C: 1.17Viscosity at 80°C: 2700 mPa-sViscosity at 700°C: 115 mPa-sNCO/OH Ratio: 1.05Stoichiometry: 95% TheoryPrepolymer Temperature: 90 to 100°CExtender Temperature: 50 to 70°CMold Temperature: 100 to 110°CPot Life: 10 to 15 minDemold: 60 min |
| Тип материала |
Категория |
Производитель |
|
Elastoflex® NA 3532/108 Resin / NA 118/4 Isocyanate |
PUR-MDI |
BASF Corporation
|
|
Xuchuan XCW-8060HT |
PUR, Unspecified |
Xuchuan Chemical (Suzhou) Co., Ltd
|
|
Xuchuan XCS-3056K |
PUR, Unspecified |
Xuchuan Chemical (Suzhou) Co., Ltd
|
|
Xuchuan XCW-6150NC |
PUR, Unspecified |
Xuchuan Chemical (Suzhou) Co., Ltd
|
|
Epoxies, Ect. 20-2390 |
PUR, Unspecified |
Epoxies, Etc.
|
|
CONATHANE® EN-4020 |
PUR, Unspecified |
Cytec Industries Inc.
|