Описание материалов:
BC 5114 is a gray low viscosity laminating system. This heat resistant resin exhibits excellent wet out, reasonable working time and may be used at room temperature without postcuring. For use above 150°F a post-cure is required. Post cure for applications requiring temperatures above 150°F can be accomplished in an oven or in use by a gradual heat rise; 2hours @ 150°F, plus 2 hours @ 250°F, plus 2 hours at 300°F. BC 5105 can afford consistent use to 300°F if required. Does not contain VCHD or MDA. Typical uses include constructing vacuum form tools, Injection and compression molds, RTM and RIM molds, and matched dies.
| Главная Информация | |
|---|
| Характеристики | - Высокая термостойкость
- Низкая вязкость
|
| Используется | |
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | | | |
| -- | 1.31 | g/cm³ | ASTM D792 |
| -- | 1.30 | g/cm³ | ASTM D1505 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore D) | 90 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение (Ultimate) | 179 | MPa | ASTM D638 |
| Flexural Strength (Break) | 228 | MPa | ASTM D790 |
| Прочность на сжатие | 364 | MPa | ASTM D695 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке (1.8 MPa, Unannealed) | 146 | °C | ASTM D648 |
| CLTE-
Поток | 2.3E-5 | cm/cm/°C | ASTM D696 |
| Термокомплект | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Компоненты термокомплекта | | | |
| Hardener | Mix Ratio by Weight: 13, Mix Ratio by Volume: 18 | | |
| Resin | Mix Ratio by Weight: 100, Mix Ratio by Volume: 100 | | |
| Срок службы горшка (24°C) | 60 | min | |
| Терморегулирующая вязкость (24°C) | 3600 | cP | ASTM D2393 |
| Время демолд | 1400 | min | |