Описание материалов:
Bayflex 952 is a fully compounded polyether-based polyurethane system consisting of two liquid components which can be water-blown. Component A is a modified diphenylmethane diisocyanate (MDI) prepolymer, and Component B is a polyether polyol system. The Bayflex 952 system is used in the manufacture of microcellular polyurethane shoe soles. Soles prepared from these components combine light weight, comfort, and durability. Processibility and dynamic flexural properties are excellent over a wide range of densities. The combination of excellent physical properties and ease of processing has made the Bayflex 952 system a prime soling material for single-density soles for fashion and casual shoes. As with any product, use of the Bayflex 952 system in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Используется | |
| Формы | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.500 | g/cm³ | Internal method |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore A) | 55 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Устойчивость к истиранию (1000 Cycles, 1000 g, H-18 Wheel) | 70.0 | mg | ASTM D4060 |
| Ross Flex-
0% рост порезов | | | ASTM D1052 |
| -29°C, 6.35 mm | > 5.0E+4 | Cycles | ASTM D1052 |
| 23°C, 6.35 mm | > 1.0E+5 | Cycles | ASTM D1052 |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Маслостойкость-
Увеличение объема | | % | ASTM D5694 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение (Break) | 3.10 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 400 | % | ASTM D412 |
| Tear Strength | | | |
| -- 1 | 4.38 | kN/m | Internal method |
| -- 2 | 14.0 | kN/m | ASTM D1004 |
| Термокомплект | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Компоненты термокомплекта 3 | | | |
| Component a | Mixing ratio by weight: 70 | | |
| Component B | Mixing ratio by weight: 100 | | |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Part A
Type: Isocyanate
Appearance: Light yellow viscous liquid
Specific Gravity @ 25°C: 1.20
Viscosity @25°C: 1100 mPa
Flash Point, PMCC: 207°C
NCO: 18.7 to 19.1 wt%
Bulk Density at 25°C: 10.01 lb/gal
Part B
Type: Polyol
Appearance: White liquid
Specific Gravity @ 25°C: 1.05
Viscosity @25°C: 1100 mPa-s
Flash Point, PMCC: 138°C
Bulk Density at 25°C: 8.70 lb/gal
Water: 0.38 wt% max
Hydroxyl Number: 157
Material Temperature: 28°CMold Temperature: 49°CDemold Time: 3.5 minLinear Shrinkage at 0.50 g/cm³: <1.0%Hand Mix Reactivity at 25°C
Cream Time: 10 to 18 sec
Tack-Free Time: 30 to 45 sec
Pull Time: 40 to 55 sec
Free-Rise Density: 15 to 18 lb/ft³ |
| Примечание |
|---|
| 1 . | Block |
| 2 . | C mould |
| 3 . | 98 Index |