Описание материалов:
PHF-8E is a certified prime grade Polypropylene specially designed for non-oriented Tubular Film EXTRUSON by Water Quench - TQ - process. PHF-8E combines excellent processability and good melt thermal stability, with films exhibiting sparkling clarity, good impact strength, easy open ability, stiffness, good barrier to fats and oils, and good chemical resistance. PHF-8E applications include film for articles requiring excellent see-through clarity such as textiles, soft goods and pastries, pre-cooked foods sterilizable bags, bags to pack cooked foods, and wrapping paper products. PHF-8E contains high slip and medium antiblock, and its recommended processing temperature is between 210° to 230°C. PHF-8E complies with FDA regulation 21CFR 177.1520 (a)(1) (b) (c)1.1, and most international regulations concerning Polypropylene use in contact with food articles.
| Главная Информация | |
|---|
| Добавка | - Высокое скольжение
- Средний антиблок
|
| Характеристики | - Приемлемый пищевой контакт
- Хорошая химическая стойкость
- Хорошая ударопрочность
- Хорошая технологичность
- Хорошая жесткость
- Хорошая термическая стабильность
- Высокая четкость
- Высокое скольжение
- Гомополимер
- Средняя антиблокировка
|
| Используется | - Сумки
- Пищевая упаковка
- Упаковка
|
| Рейтинг агентства | - FDA 21 CFR 177,1520 (a) 1
- FDA 21 CFR 177,1520 (b)
- FDA 21 CFR 177,1520 (c) 1,1
|
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.907 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (230°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Флекторный модуль-
1% Secant (Injection Molded) | 1550 | MPa | ASTM D790 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Сектантный модуль 1 | | | ASTM D882 |
| 1% Secant, MD
: 32 µm | 689 | MPa | |
| 1% Secant, TD
: 32 µm | 689 | MPa | |
| Прочность на растяжение 2 | | | ASTM D882 |
| MD
: Break, 32 µm | 55.2 | MPa | |
| TD
: Break, 32 µm | 37.9 | MPa | |
| Удлинение при растяжении 3 | | | ASTM D882 |
| MD
: Break, 32 µm | 500 | % | |
| TD
: Break, 32 µm | 550 | % | |
| Elmendorf Tear Strength 4 | | | ASTM D1922 |
| MD
: 32 µm | 40 | g | |
| TD
: 32 µm | 40 | g | |
| Spencer Impact 5(31.8 µm) | 400 | g | ASTM D3420 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блеск 6(45°, 31.8 µm) | 85 | | ASTM D2457 |
| Haze 7(31.8 µm) | 2.0 | % | ASTM D1003 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | 210 to 230 | °C | |
| Примечание |
|---|
| 1 . | 1.25 mils (31 µm) film, melt temperature 410-450°F (210-230°C), blow-up-ratio 1.5:1 |
| 2 . | 1.25 mils (31 µm) film, melt temperature 410-450°F (210-230°C), blow-up-ratio 1.5:1 |
| 3 . | 1.25 mils (31 µm) film, melt temperature 410-450°F (210-230°C), blow-up-ratio 1.5:1 |
| 4 . | 1.25 mils (31 µm) film, melt temperature 410-450°F (210-230°C), blow-up-ratio 1.5:1 |
| 5 . | 1.25 mils (31 µm) film, melt temperature 410-450°F (210-230°C), blow-up-ratio 1.5:1 |
| 6 . | 1.25 mils (31 µm) film, melt temperature 410-450°F (210-230°C), blow-up-ratio 1.5:1 |
| 7 . | 1.25 mils (31 µm) film, melt temperature 410-450°F (210-230°C), blow-up-ratio 1.5:1 |