DOW™ LLDPE DFDA-7059 NT 7
| Категория | LLDPE, Linear Low Density Polyethylene Resin |
| Производитель | The Dow Chemical Company |
| Торговая марка | DOW™ LLDPE |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
izCQsV_DOW-LLDPE-DFDA-7059-NT-7.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
DOW DFDA-7059 NT 7 linear low density polyethylene resin is an ethylene-butene copolymer supplied in pellet form. Generally speaking, the resin is suitable for film processing with thin casting thickness, and these applications require transparency and toughness. The resin has excellent performance in the processing of co-extrusion cast stretch film. The resin is also suitable for the processing of drip irrigation equipment, hoses and pipe fittings.
Main features:
Complies with:
Main features:
- High transparency
- High tensile strength
- high elongation
- good puncture strength
Complies with:
- Comply with the requirements of U.S. Food and Drug Administration Regulation 21 CFR 177.1520(c) 3.2a.
- EU, No 10/2011
- Candaian HPFB No Objection
| Главная Информация | |
|---|---|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Удельный вес | 0.918 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Прочность на растяжение 1 | ASTM D638 | ||
| Yield | 9.51 | MPa | ASTM D638 |
| Fracture | 10.3 | MPa | ASTM D638 |
| Удлинение при растяжении 2 | ASTM D638 | ||
| Yield | 11 | % | ASTM D638 |
| Fracture | 570 | % | ASTM D638 |
| Флекторный модуль- 2% Secant 3 | 221 | MPa | ASTM D790B |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 25 | µm | |
| Прочность на растяжение | ASTM D882 | ||
| MD : Broken, 25 µm, extruded film | 34.5 | MPa | ASTM D882 |
| TD : Broken, 25 µm, extruded film | 24.8 | MPa | ASTM D882 |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Broken, 25 µm, extruded film | 450 | % | ASTM D882 |
| TD : Broken, 25 µm, extruded film | 850 | % | ASTM D882 |
| Ударное падение Dart (25 µm, Cast Film) | 70 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 25 µm, cast film | 50 | g | ASTM D1922 |
| TD : 25 µm, cast film | 400 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Температура плавления (DSC) | 125 | °C | Internal method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45, 25.4 µm, cast film) | 92 | ASTM D2457 | |
| Haze (25.4 µm, Cast Film) | 2.5 | % | ASTM D1003 |
| Дополнительная информация |
|---|
| 在 520°F (270°C) 下挤出的槽型铸造薄膜具有典型的薄膜属性。 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Температура расплава | 271 | °C |
| Инструкции по экструзии |
|---|
| 铸造薄膜的制造条件： 可采用传统的槽型铸造薄膜挤出设备进行挤压，只需进行微小的机器改造以获得最佳使用效果。 熔体温度：520°F (270°C) |
| Примечание | |
|---|---|
| 1 . | Plaque molded and tested in accordance with ASTM D4976. |
| 2 . | Plaque molded and tested in accordance with ASTM D4976. |
| 3 . | Plaque molded and tested in accordance with ASTM D4976. |
| Тип материала | Категория | Производитель |
|---|---|---|
| CERTENE™ LLBF-122D | LLDPE | Muehlstein |
| Evolue™ SP2320H | LLDPE | Prime Polymer Co., Ltd. |
| DOW™ Electrical & Telecommunications DFDA-1375 RD | LLDPE | The Dow Chemical Company |
| Hanwha Total PE 4222F | LLDPE | HANWHA TOTAL PETROCHEMICALS Co., Ltd. |
| Jam 22501KJ | LLDPE | Jam Petrochemical Company |
| Braskem PE SLH0820/30AF | LLDPE | Braskem |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved