Versaflex™ HC 2110-35N

Категория	TPE, Thermoplastic Elastomer
Производитель	PolyOne Corporation
Торговая марка	Versaflex™
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	ibUIQ7_Versaflex-HC-2110-35N.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

Versaflex™ HC 2110-35N is a thermoplastic elastomer developed as an alternative to traditional isoprene rubber solutions for infusion stoppers & septums that require multiple needle penetration with good resealing performance. Versaflex™ HC 2110-35N addresses needs such as low piercing force and good spike retention.
- Overmolds to PP and PE
- Approved to ISO 10993-4 & -5
- Approved to USP VI
- Approved to USP 381: Elastomeric closures for injection.

Главная Информация
Характеристики	Хорошая дезинфекция Хорошая производительность формования Хорошая стабильность обработки Хорошая мобильность Хорошая окраска Хорошая производительность при потере
Используется	Формовочная форма для облицовки Штепсельная Вилка Уплотнение Уплотнительное устройство Мембрана Медицинские принадлежности/принадлежности для ухода
Рейтинг агентства	ISO 10993 4 часть 2 ISO 10993 часть 5 USP категория VI
Соответствие RoHS	Соответствие RoHS
Внешний вид	Натуральный цвет
Формы	Частицы
Метод обработки	Литье под давлением

Физический	Номинальное значение	Единица измерения	Метод испытания
Удельный вес	0.898	g/cm³	ASTM D792

Твердость	Номинальное значение	Единица измерения	Метод испытания
Твердость дюрометра (Shore A, 10 sec)	34		ASTM D2240

Эластомеры	Номинальное значение	Единица измерения	Метод испытания
Tensile Stress (100% Strain, 23°C)	0.689	MPa	ASTM D412
Прочность на растяжение (Break, 23°C)	2.76	MPa	ASTM D412
Удлинение при растяжении (Break, 23°C)	620	%	ASTM D412
Tear Strength	17	kN/m	ISO 34-1
Комплект сжатия			ISO 815
23°C, 72 hr	19	%	ISO 815
70°C, 22 hr	33	%	ISO 815
100°C, 22 hr	47	%	ISO 815

Анализ заполнения	Номинальное значение	Единица измерения	Метод испытания
Видимая вязкость (200°C, 11200 sec^-1)	11.0	Pa·s	ASTM D3835

Инъекция	Номинальное значение	Единица измерения
Рекомендуемый Макс измельчения	20	%
Задняя температура	182 - 193	°C
Средняя температура	221 - 238	°C
Передняя температура	238 - 249	°C
Температура сопла	238 - 249	°C
Температура обработки (расплава)	232 - 249	°C
Температура формы	15.6 - 32.2	°C
Back Pressure	0.00 - 0.552	MPa
Screw Speed	80 - 200	rpm

Инструкции по впрыску
Color concentrates with polypropylene (PP), ethylene vinyl acetate (EVA), or polyethylene (PE) carriers are most suitable for coloring Versaflex™ HC 2110-35N. Improved color dispersion can be achieved by using higher melt flow concentrates (with a melt flow from 25 - 40 g/10 min). Typical loadings for color concentrates are 1% to 5% by weight. Liquid color can be used, but mineral oil based carriers may have a significant effect on the final hardness value. Concentrates based on PVC should not be used. A high color match consistency can be obtained by using precolored compounds available from GLS. The final determination of color concentrate suitability should be determined by customer trials.Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).Regrind levels up to 20% can be used with Versaflex™ HC 2110-35N with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer.Versaflex™ HC 2110-35N has excellent melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer.Drying is not RequiredInjection Speed: 1 to 3 in/sec1st Stage - Boost Pressure: 800 to 1200 psi2nd Stage - Hold Pressure: 40-70% of BoostHold Time (Thick Part): 2 to 5 secHold Time (Thin Part): 1 to 4 sec

Инструкции по впрыску

Color concentrates with polypropylene (PP), ethylene vinyl acetate (EVA), or polyethylene (PE) carriers are most suitable for coloring Versaflex™ HC 2110-35N. Improved color dispersion can be achieved by using higher melt flow concentrates (with a melt flow from 25 - 40 g/10 min). Typical loadings for color concentrates are 1% to 5% by weight. Liquid color can be used, but mineral oil based carriers may have a significant effect on the final hardness value. Concentrates based on PVC should not be used. A high color match consistency can be obtained by using precolored compounds available from GLS. The final determination of color concentrate suitability should be determined by customer trials.Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).Regrind levels up to 20% can be used with Versaflex™ HC 2110-35N with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer.Versaflex™ HC 2110-35N has excellent melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer.Drying is not RequiredInjection Speed: 1 to 3 in/sec1st Stage - Boost Pressure: 800 to 1200 psi2nd Stage - Hold Pressure: 40-70% of BoostHold Time (Thick Part): 2 to 5 secHold Time (Thin Part): 1 to 4 sec

Тип материала	Категория	Производитель
Maxelast® C4990	TPE	Nantong Polymax Elastomer Technology, Co., Ltd
Maxelast® P2665	TPE	Nantong Polymax Elastomer Technology, Co., Ltd
PRIMALLOY® B1600	TPE	Mitsubishi Chemical Performance Polymers, Inc.
Monprene® SP-12251	TPE	Teknor Apex Company
Mediprene® 502534M	TPE	ELASTO
Monprene® CP-18250 (PRELIMINARY DATA)	TPE	Teknor Apex Company

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

