SABIC® LDPE 2404N0
| Категория | LDPE, Low Density Polyethylene |
| Производитель | Saudi Basic Industries Corporation (SABIC) |
| Торговая марка | SABIC® LDPE |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
iQMsXU_SABIC-LDPE-2404N0.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
SABIC® LDPE 2404N0 is a LDPE tubular grade without additives. The product is typically developed for cast film extrusion applications requiring an optimal relationship between draw down, purity and organoleptic properties.
Application
SABIC® LDPE 2404N0 is typically suitable for a wide variety of cast film application.
This product is not intended for and must not be used in any pharmaceutical/medical applications.
Application
SABIC® LDPE 2404N0 is typically suitable for a wide variety of cast film application.
This product is not intended for and must not be used in any pharmaceutical/medical applications.
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.925 | g/cm³ | ISO 1183/A |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 4.2 | g/10 min | ISO 1133 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Модуль растяжения (1.10mm, molded) | 250 | MPa | ISO 527-2/50 |
| Tensile Stress (fracture, 1.10mm, molded) | 12.0 | MPa | ISO 527-2/50 |
| Растяжимое напряжение | ISO 527-2/50 | ||
| Yield, 1.10mm, molded | 11 | % | ISO 527-2/50 |
| Fracture, 1.10mm, molded | 800 | % | ISO 527-2/50 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Викат Температура размягчения | 94.0 | °C | ISO 306/A |
| Температура плавления (DSC) | 111 | °C | Internal method |
| Enthalpy Change | 134 | J/g | Internal method |
| Дополнительная информация |
|---|
| Mechanical properties have been determined on compression moulded test specimen (1,1 mm thick and 5,0 mm wide) at 50 mm/min. |
| Тип материала | Категория | Производитель |
|---|---|---|
| PrimaFlex® LD 19009 | LDPE | Plastic Solutions, Inc. |
| SABIC® LDPE 2402H3W | LDPE | Saudi Basic Industries Corporation (SABIC) |
| SABIC® LDPE 2801H0W | LDPE | Saudi Basic Industries Corporation (SABIC) |
| SABIC® LDPE HP4023W | LDPE | SABIC Americas, Inc. |
| Petrothene® NA443 (Blown) | LDPE | LyondellBasell Industries |
| SABIC® LDPE PCG09 | LDPE | Saudi Basic Industries Corporation (SABIC) |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved