Описание материалов:
SABIC® PP FPH50 is a grade developed for thin wall packaging as well as the caps & closures market. The grade is nucleated and is characterised by a high crystallisation temperature, excellent flow behaviour in combination with a high stiffness. SABIC® PP FPH50 allows for very cost efficient processing on the basis of easy mould filling, very short cycle times and robust processing behaviour in combination with pigments. It has a very good antistatic performance and shows easy demoulding.
SABIC® PP FPH50 is typically used in thin wall packing applications both for food and non-food segments. In caps and closure, the grade could be used for wide mouth caps, amongst others. In media packaging, the grade offers opportunities for cycle time optimisation. The grade has excellent heat deflection temperature making it particularly suitable for hot fill applications.
This product is not intended for and must not be used in any pharmaceutical/medical applications.
| Главная Информация | |
|---|
| Добавка | - Антистатический
- Нуклеативный агент
|
| Характеристики | - Антистатический
- Цикл быстрого формования
- Хороший поток
- Хороший выпуск пресс-формы
- Высокая жесткость
- Гомополимер
- Ядро
|
| Используется | - Колпачки
- Затворы
- Пищевая упаковка
- Медиа упаковка
- Упаковка
- Тонкостенная упаковка
|
| Номер файла UL | |
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Массовый расход расплава (MFR) (230°C/2.16 kg) | 50 | g/10 min | ASTM D1238, ISO 1133 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale) | 114 | | ASTM D785 |
| Твердость по суше (Shore D) | 71 | | ISO 868 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | | | |
| 1% Secant 1 | 2100 | MPa | ASTM D638 |
| -- | 2050 | MPa | ISO 527-2/1A/1 |
| Прочность на растяжение | | | |
| Yield 2 | 40.0 | MPa | ASTM D638 |
| Yield | 39.0 | MPa | ISO 527-2/1A/50 |
| Удлинение при растяжении | | | |
| Yield 3 | 7.0 | % | ASTM D638 |
| Yield | 7.0 | % | ISO 527-2/1A/50 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность (23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Зубчатый изод Impact | | | |
| 23°C | 25 | J/m | ASTM D256A |
| 23°C | 2.5 | kJ/m² | ISO 180/1A |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | |
| 0.45 MPa, Unannealed | 110 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 105 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 65.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 60.0 | °C | ISO 75-2/Af |
| Викат Температура размягчения | | | |
| -- | 154 | °C | ASTM D1525, ISO 306/A120 6 6 |
| -- | 103 | °C | ASTM D1525, ISO 306/B120 7 7 |
| Примечание |
|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |