Andur M-11 (97% HQEE/ 3% TMP)
Описание материалов:
Andur M-11 is an MDI-Ester prepolymer that, when processed with close attention to handling procedures and formulation, produces high quality elastomers. These elastomers perform very well in dynamic applications.
| Твердость | Номинальное значение | | Метод испытания |
|---|
| Твердость дюрометра | | | ASTM D2240 |
| Shaw A | 99 | | ASTM D2240 |
| Shaw D | 60 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на сжатие | | | ASTM D695 |
| 2% strain | 3.79 | MPa | ASTM D695 |
| 5% strain | 6.89 | MPa | ASTM D695 |
| 10% strain | 10.3 | MPa | ASTM D695 |
| 15% strain | 13.8 | MPa | ASTM D695 |
| 20% strain | 17.2 | MPa | ASTM D695 |
| 25% strain | 22.1 | MPa | ASTM D695 |
| 50% strain | 67.6 | MPa | ASTM D695 |
| Устойчивость к истиранию | 47.6 | mg | ASTM D1044 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ASTM D412 |
| 100% strain | 22.1 | MPa | ASTM D412 |
| 200% strain | 22.8 | MPa | ASTM D412 |
| 300% strain | 21.7 | MPa | ASTM D412 |
| Прочность на растяжение (Yield) | 24.1 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 350 | % | ASTM D412 |
| Комплект сжатия | 33 | % | ASTM D395 |
| Термокомплект | Номинальное значение | Единица измерения | |
|---|
| Срок службы горшка | 6.0 - 8.0 | min | |
| Время демолд | 80 | min | |
| Дополнительная информация |
|---|
| Die C Tear, ASTM D1004: 900 pliAverage Split Tear, ASTM D1938: 600 pliStoichiometry Curative Level: 90%Parts of curative per 100 parts Andur M-11, 8.9% NCO: 18.76 parts by weightParts of curative per 100 parts Andur M-11, 9% NCO: 18.97 parts by weightParts of curative per 100 parts Andur M-11, 9.1% NCO: 19.18 parts by weightParts of curative per 100 parts Andur M-11, 9.2% NCO: 19.38 parts by weightMix Temperature:
Andur M-11: 212°F
Curative HQEE/TMP: 230°F
Stability:
Ambient Temperature, 25°C: 6 Months
Melting Temperature, 60°C: 1 Month
Processing Temperature, 90°C: 12 Hours
Processing Temperature, 105°C: 3 Hours |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 110 - 140 | °C | |