LUVOCOM® 80/CF/12/TF/10/GY

Категория POM, Acetal (POM) Copolymer
Производитель Lehmann & Voss & Co.
Торговая марка LUVOCOM®
Порт Китай Шанхайский порт
Торговые условия FOB, CFR, CIF
Платежное средство L/C, T/T, Western Union
PDF hzoRsB_LUVOCOM-80-CF-12-TF-10-GY.pdf
Контактная информация
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Описание материалов:
LUVOCOM®80/CF/12/TF/10/GY is a polyoxymethylene (POM) copolymer material, and the filler is 12% carbon fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main characteristics of 80/CF/12/TF/10/GY are:
  • flame retardant/rated flame
  • Conductivity
  • Electrostatic protection
  • Wear-resistant
  • Lubrication

Typical application areas include:
  • engineering/industrial accessories
  • textile/fiber
  • Automotive Industry
  • business/office supplies
Главная Информация
Наполнитель/армирование
  • Армированный углеродным волокном материал, 12% наполнитель по весу
Добавка
  • PTFE лубрикант (10%)
Характеристики
  • Проводящий
  • Низкий коэффициент трения
  • Защита от электростатического разряда
  • Хорошая стойкость к истиранию
  • Смазка
Используется
  • Шестерня
  • Текстильные изделия
  • Инженерные аксессуары
  • Применение в автомобильной области
  • Бизнес-оборудование
  • Камера
  • Подшипник
Внешний вид
  • Серый
ФизическийНоминальное значениеЕдиница измеренияМетод испытания
Плотность 1.54g/cm³ISO 1183
Плавкий объем-расход (MVR) (190°C/5.0 kg)12.0cm³/10minISO 1133
Формовочная усадка 0.30 - 0.70%DIN 16901
Поглощение воды (23°C, 24 hr)< 0.10%
МеханическиеНоминальное значениеЕдиница измеренияМетод испытания
Модуль растяжения 8000MPaISO 527-2
Tensile Stress (Break)85.0MPaISO 527-2
Растяжимое напряжение (Yield)2.5%ISO 527-2
Флекторный модуль 6000MPaISO 178
Флекторный стресс 125MPaISO 178
Коэффициент трения
    Dynamic 0.15
    Static 0.11
Flexural Strain at Flexural Strength 3.2%ISO 178
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Максимальная рабочая температура- Короткий срок 120°C
ЭлектрическийНоминальное значениеЕдиница измеренияМетод испытания
Insulation Resistance ohmsIEC 60167
ВоздействиеНоминальное значениеЕдиница измеренияМетод испытания
Charpy Unnotched Impact Strength (23°C)25kJ/m²ISO 179/1eU
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Температура непрерывного использования 100°CUL 746B
Викат Температура размягчения 160°CISO 306/A
CLTE- Поток 6.0E-5cm/cm/°CDIN 53752
Теплопроводность 0.40W/m/KDIN 52612
ЭлектрическийНоминальное значениеЕдиница измеренияМетод испытания
Удельное сопротивление поверхности < 1.0E+6ohmsIEC 60093
ВоспламеняемостьНоминальное значениеЕдиница измеренияМетод испытания
Огнестойкость HBUL 94
ИнъекцияНоминальное значениеЕдиница измерения
Температура сушки
    A 75.0°C
    Dehumidification desiccant, B 120°C
Время сушки
    A 2.0 - 8.0hr
    Dehumidification desiccant, B 2.0 - 4.0hr
Задняя температура 175 - 190°C
Средняя температура 185 - 205°C
Передняя температура 180 - 200°C
Температура сопла 175 - 200°C
Температура обработки (расплава) 200°C
Температура формы 80.0 - 120°C
Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information If originally sealed containers are used, it is normally possible to omit the predrying stage. If PTFE materials are not predried, an increase in deposits inside the mould may occur. When changing from higher melting-point polymers such as polyamides to this product, extremely thorough intermediate cleaning should be carried out. Processing temperatures above 215°C may very rapidly cause thermal damage and should therefore be avoided, particularly as formaldehyde may be eliminated here. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.
Тип материала Категория Производитель
RTP 800 TFE 20 SI 2 Acetal (POM) Copolymer RTP Company
Kepital® F20-02 Acetal (POM) Copolymer Korea Engineering Plastics Co., Ltd
LNP™ THERMOCOMP™ KZ001L compound Acetal (POM) Copolymer SABIC Innovative Plastics
Cheng Yu FV30725 Acetal (POM) Homopolymer Cheng Yu Plastic Company Limited
Quadrant EPP ERTACETAL® H Acetal (POM) Homopolymer Quadrant Engineering Plastic Products
Edgetek™ AT-30GF/000 BLACK Acetal (POM) Copolymer PolyOne Corporation
Получите информацию об этом продукте следующим способом.
Телефон+086 13424755533
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Copyright © russianpolymer.com All Rights Reserved
Получите информацию об этом продукте следующим способом.
+08613424755533
sales@su-jiao.com

Служба поддержки клиентов Вичат
Свяжитесь с нами