TOTAL Polyethylene Lotrène® Q1018 N
Описание материалов:
Lotrène ® Q1018 N is an ethylene-butene copolymer produced in a gas phase reactor. It is designed for delivering competitive performance in most blown film applications.
Lotrène ® Q1018 N can be processed at high output rates with moderate extrusion pressure, good bubble stability and gauge control on blown film machine designed for LLDPE.
Lotrène ® Q1018 N can advantageously be blended with LDPE or other PE resins used in blown film mono extrusion or coextrusion to improve film properties.
Lotrène ® Q1018 N is suited for many applications in the field of consumer, industrial, food or hygiene packaging such as collation shrink, liners, Form-Fill-Seal, heavy-duty sacks, refuse sacks or other bags and non-packaging applications like agricultural films e.g. tunnel and mulching films.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Бутене комномер
- Устойчивость к окислению
|
| Используется | - Упаковка
- Пленка
- Подкладка
- Сумка
- Промышленное применение
- Сельскохозяйственное применение
- Пищевая упаковка
- Усадочная пленка
- Тяжелая упаковочная сумка
|
| Метод обработки | - Экструзионная пленка
- Выдувная пленка
- Коэкструзионное формование
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 0.918 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 40 | µm | |
| Модуль растяжения | | | ISO 178 |
| 1% secant, MD
: 40 µm, blown film | 215 | MPa | ISO 178 |
| 1% secant, TD
: 40 µm, blown film | 245 | MPa | ISO 178 |
| Tensile Stress | | | ISO 527-3 |
| MD
: Yield, 40 µm, blown film | 11.0 | MPa | ISO 527-3 |
| TD
: Yield, 40 µm, blown film | 11.0 | MPa | ISO 527-3 |
| MD
: Broken, 40 µm, blown film | 38.0 | MPa | ISO 527-3 |
| TD
: Broken, 40 µm, blown film | 33.0 | MPa | ISO 527-3 |
| Удлинение при растяжении | | | ISO 527-3 |
| MD
: Broken, 40 µm, blown film | 800 | % | ISO 527-3 |
| TD
: Broken, 40 µm, blown film | 850 | % | ISO 527-3 |
| Ударное падение Dart 1(40 µm, Blown Film) | 150 | g | ISO 7765-1 |
| Elmendorf Tear Strength | | | ISO 6383-2 |
| MD
: 40.0 µm | 70.0 | kN/m | ISO 6383-2 |
| TD
: 40.0 µm | 120.0 | kN/m | ISO 6383-2 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Викат Температура размягчения 2 | 100 | °C | ASTM D1525 |
| Температура плавления | 122 | °C | Internal method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блеск (45°, 40.0 µm, Blown Film) | 60 | | ASTM D2457 |
| Haze (40.0 µm, Blown Film) | 11 | % | ISO 14782 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | 180 - 220 | °C | |
| Инструкции по экструзии |
|---|
| BUR: 2:1 to 3:1Die gap: > 1.8 mmFilm figures are obtained using laboratory test specimens produced with the following extrusion conditions: 45 mm screw, L/D = 30, die = 120 mm, die gap = 2.2 mm, BUR = 2.5:1, temperature = 210°C. |