Описание материалов:
Eastar™ Copolyesters are brilliantly clear polymers that have excellent impact strength, chemical resistance, dimensional stability, and low shrinkage rates. Eastar™ MN004 contains a mold release.
This product has been GREENGUARD INDOOR AIR QUALITY CERTIFIED®.
The GREENGUARD INDOOR AIR QUALITY CERTIFIED® Mark is a registered certification mark used under license through the GREENGUARD Environmental Institute (GEI). GEI is an industry-independent, non-profit organization that oversees the GREENGUARD Certification Program. The GREENGUARD Certification Program is an industry independent, third-party testing program for low-emitting products and materials for indoor environments. For more information about GEI and to obtain printable certificates for Eastman™ Copolyesters, visit www.greenguard.org. Choose Eastman Chemical Company under the Manufacturer category and click search to display a list of our products.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Хорошая химическая стойкость
- Хорошая стабильность размеров
- Хорошая ударопрочность
- Хороший выпуск пресс-формы
- Высокая четкость
- Низкая усадка
|
| Используется | - Медицинские/медицинские приложения
|
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | | | |
| -- | 1.23 | g/cm³ | ASTM D792 |
| 23°C | 1.23 | g/cm³ | ISO 1183 |
| Формовочная усадка-
Поток (3.20 mm) | 0.20 to 0.50 | % | ASTM D955 |
| Поглощение воды (23°C, 24 hr) | 0.13 | % | ASTM D570, ISO 62 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла (R-Scale, 23°C) | 105 | | ASTM D785 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение | | | |
| Yield, 23°C | 45.0 | MPa | ASTM D638 |
| Yield, 23°C, 4.00 mm | 46.0 | MPa | ISO 527-2 |
| Break, 23°C | 52.0 | MPa | ASTM D638 |
| Break, 23°C, 4.00 mm | 47.0 | MPa | ISO 527-2 |
| Удлинение при растяжении | | | |
| Yield, 23°C | 5.0 | % | ASTM D638 |
| Yield, 23°C, 4.00 mm | 4.4 | % | ISO 527-2 |
| Break, 23°C | 330 | % | ASTM D638 |
| Break, 23°C, 4.00 mm | 230 | % | ISO 527-2 |
| Флекторный модуль | | | |
| 23°C | 1800 | MPa | ASTM D790 |
| 23°C, 4.00 mm | 1800 | MPa | ISO 178 |
| Флекторный стресс | | | |
| 23°C, 4.00 mm | 63.0 | MPa | ISO 178 |
| Yield, 23°C | 66.0 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | | | |
| -40°C | 64 | J/m | ASTM D256 |
| 23°C | No Break | | ASTM D256 |
| -40°C | 7.4 | kJ/m² | ISO 180 |
| 23°C | 130 | kJ/m² | ISO 180 |
| Незубчатый изод Impact | | | ASTM D4218 |
| -40°C | No Break | | |
| 23°C | No Break | | |
| Многоосная инструментальная Энергия удара | | | ISO 6603-2 |
| -40°C, Energy to Peak Force | 16.0 | J | |
| 23°C, Energy to Peak Force | 14.0 | J | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | |
| 0.45 MPa, Unannealed | 74.0 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 64.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed | 65.0 | °C | ISO 75-2/A |
| Викат Температура размягчения | | | |
| -- | 88.0 | °C | ASTM D1525, ISO 306/A 2 1 |
| -- | 79.0 | °C | ISO 306/B |
| Удельный нагрев | | | DSC |
| 60°C | 1340 | J/kg/°C | |
| 240°C | 2050 | J/kg/°C | |
| Теплопроводность (23°C) | 0.19 | W/m/K | ASTM C177 |
| Воспламеняемость | Номинальное значение | | Метод испытания |
|---|
| Огнестойкость | | | UL 94 |
| 1.60 mm | HB | | |
| 3.20 mm | HB | | |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Коэффициент пропускания | | | ASTM D1003 |
| Total | 89.0 | % | |
| Regular | 87.0 | % | |
| Haze | < 1.0 | % | ASTM D1003 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 75.0 | °C | |
| Время сушки | 6.0 | hr | |
| Температура обработки (расплава) | 250 to 270 | °C | |
| Температура формы | 15.0 to 40.0 | °C | |
| Примечание |
|---|
| 1 . | Loading 1 (10 N) |