Riblene® FF 30
| Категория | LDPE, Low Density Polyethylene |
| Производитель | Versalis S.p.A. |
| Торговая марка | Riblene® |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
gcG4if_Riblene-FF-30.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
Riblene FF 30 is a high molecular weight low density polyethylene (LDPE), suitable for blown film extrusion.
Riblene FF 30 is characterised by a good melt strength leading to a good bubble stability during extrusion.
Films manufactured by Riblene FF 30 are easily heat shrinkable and characterised by good optical and mechanical properties.
Main Application
Riblene FF 30 is recommended for the production of shrink film for medium and light loads, for lamination film and for blend.
Riblene FF 30 is characterised by a good melt strength leading to a good bubble stability during extrusion.
Films manufactured by Riblene FF 30 are easily heat shrinkable and characterised by good optical and mechanical properties.
Main Application
Riblene FF 30 is recommended for the production of shrink film for medium and light loads, for lamination film and for blend.
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Рейтинг агентства |
|
| Формы |
|
| Метод обработки |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Плотность | 0.923 | g/cm³ | ISO 1183 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.80 | g/10 min | ISO 1133 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Коэффициент трения (vs. Itself - Dynamic, Blown Film) | > 0.50 | ISO 8295 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 70 | µm | |
| Толщина пленки-рекомендовано/доступно | 30 to 120 µm | ||
| Модуль растяжения | ISO 527-3 | ||
| 1% Secant, MD : 70 µm, Blown Film | 180 | MPa | |
| 1% Secant, TD : 70 µm, Blown Film | 190 | MPa | |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 70 µm, Blown Film | 10.0 | MPa | |
| TD : Yield, 70 µm, Blown Film | 11.0 | MPa | |
| MD : Break, 70 µm, Blown Film | 22.0 | MPa | |
| TD : Break, 70 µm, Blown Film | 19.0 | MPa | |
| Удлинение при растяжении | ISO 527-3 | ||
| MD : Break, 70 µm, Blown Film | 380 | % | |
| TD : Break, 70 µm, Blown Film | 600 | % | |
| Ударное падение Dart 1(70 µm, Blown Film) | 180 | g | ISO 7765-1 |
| Elmendorf Tear Strength 2 | ISO 6383-2 | ||
| MD : 70.0 µm | 45.0 | kN/m | |
| TD : 70.0 µm | 60.0 | kN/m |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Температура ломкости | < -75.0 | °C | ASTM D746 |
| Викат Температура размягчения | 95.0 | °C | ISO 306/A |
| Температура плавления | 113 | °C | Internal Method |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Блеск (45°, 70.0 µm, Blown Film) | 65 | ASTM D2457 | |
| Haze (70.0 µm, Blown Film) | 8.0 | % | ISO 14782 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|---|---|---|
| Температура расплава | 170 to 200 | °C |
| Примечание | |
|---|---|
| 1 . | F50 |
| 2 . | Blown Film |
| Тип материала | Категория | Производитель |
|---|---|---|
| Sinpolene MBW1322/T | LDPE | Teknor Apex Asia Pacific PTE. LTD. |
| Polymer-E M5100 | LDPE | Asia Polymer Corporation (APC) |
| RTP ESD A 700 A | LDPE | RTP Company |
| SABIC® LDPE PCG02 | LDPE | Saudi Basic Industries Corporation (SABIC) |
| MIRASON™ 68 | LDPE | Mitsui Chemicals, Inc. |
| Trithene® TS 7028 | LDPE | Petroquimica Triunfo |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved