Описание материалов:
Vydyne 49H is general-purpose, impact-modified PA66 resin. Available in natural, it is heat-stabilized for improved resistance to elevated temperatures. The heat stabilization package for Vydyne 49H was formulated to provide thermal endurance when used in applications in which continuous or extended high-temperature exposure is anticipated.
Vydyne 49H is recognized for all the processing and property advantages inherent to PA66 with the addition of improved impact strength. This resin offers a well balanced combination of engineering properties characterized by high melt point, good surface lubricity, abrasion resistance and resistance to many chemicals, machine and motor oils, solvents and gasoline.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Сопротивление бензину
- Общее назначение
- Хорошая стойкость к истиранию
- Хорошая химическая стойкость
- Хорошая технологичность
- Хорошая прочность
- Высокая ударопрочность
- Модификация удара
- Прочность при низкой температуре
- Маслостойкий
- Устойчивость к растворителям
|
| Используется | - Автомобильные Приложения
- Разъемы
- Потребительские приложения
- Электрическое/электронное применение
- Крепежные детали
- Шестерни
- Общее назначение
- Промышленное применение
|
| Рейтинг агентства | - Астм д 4066 PA0161
- Астм д 6779 PA0161
|
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Физический | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Плотность | 1.11 | -- | g/cm³ | ISO 1183 |
| Формовочная усадка | | | | ISO 294-4 |
| Across Flow
: 2.00 mm | 1.6 | -- | % | |
| Flow
: 2.00 mm | 1.8 | -- | % | |
| Поглощение воды | | | | ISO 62 |
| 23°C, 24 hr | 1.3 | -- | % | |
| Equilibrium, 50% RH | 2.3 | -- | % | |
| Механические | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Модуль растяжения | 3040 | 2130 | MPa | ISO 527-2 |
| Tensile Stress | | | | ISO 527-2 |
| Yield | 70.0 | 50.0 | MPa | |
| Break | 46.0 | 42.0 | MPa | |
| Растяжимое напряжение (Break) | 17 | 40 | % | ISO 527-2 |
| Флекторный модуль | 2600 | 890 | MPa | ISO 178 |
| Флекторный стресс | 81.0 | 27.0 | MPa | ISO 178 |
| Воздействие | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Ударная прочность | | | | ISO 179 |
| -40°C | 8.0 | 6.0 | kJ/m² | |
| -30°C | 11 | 10 | kJ/m² | |
| 23°C | 13 | 43 | kJ/m² | |
| Charpy Unnotched Impact Strength | | | | ISO 179 |
| -30°C | No Break | No Break | | |
| 23°C | No Break | No Break | | |
| Зубчатый изод ударная прочность | | | | ISO 180 |
| -40°C | 8.0 | 10 | kJ/m² | |
| -30°C | 9.0 | 15 | kJ/m² | |
| 23°C | 10 | 37 | kJ/m² | |
| Тепловой | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature | | | | |
| 0.45 MPa, Unannealed | 202 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 69.0 | -- | °C | ISO 75-2/A |
| Температура плавления | 260 | -- | °C | ISO 11357-3 |
| CLTE | | | | ISO 11359-2 |
| Flow
: 23 to 55°C, 2.00 mm | 8.6E-5 | -- | cm/cm/°C | |
| Transverse
: 23 to 55°C, 2.00 mm | 1.2E-4 | -- | cm/cm/°C | |
| RTI Elec | | | | UL 746 |
| 0.750 mm | 130 | -- | °C | |
| 1.50 mm | 130 | -- | °C | |
| 3.00 mm | 130 | -- | °C | |
| RTI Imp | | | | UL 746 |
| 0.750 mm | 75.0 | -- | °C | |
| 1.50 mm | 75.0 | -- | °C | |
| 3.00 mm | 75.0 | -- | °C | |
| RTI Str | | | | UL 746 |
| 0.750 mm | 110 | -- | °C | |
| 1.50 mm | 110 | -- | °C | |
| 3.00 mm | 110 | -- | °C | |
| Электрический | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Сопротивление громкости (0.750 mm) | 1.0E+11 | -- | ohms·cm | IEC 60093 |
| Диэлектрическая прочность (1.00 mm) | 14 | -- | kV/mm | ASTM D149 |
| Дуговое сопротивление (3.00 mm) | PLC 6 | -- | | ASTM D495 |
| Comparative Tracking Index (3.00 mm) | 525 | -- | V | IEC 60112 |
| Высокоусиленное дуговое зажигание (HAI) | | | | UL 746 |
| 0.750 mm | PLC 0 | -- | | |
| 1.50 mm | PLC 0 | -- | | |
| 3.00 mm | PLC 0 | -- | | |
| Высоковольтная скорость отслеживания дуги (HVTR) | PLC 2 | -- | | UL 746 |
| Зажигание горячей проволоки (HWI) | | | | UL 746 |
| 0.750 mm | PLC 4 | -- | | |
| 1.50 mm | PLC 4 | -- | | |
| 3.00 mm | PLC 3 | -- | | |
| Воспламеняемость | Сухой | Состояние | Единица измерения | Метод испытания |
|---|
| Огнестойкость | | | | UL 94 |
| 0.750 mm | HB | -- | | |
| 1.50 mm | HB | -- | | |
| 3.00 mm | HB | -- | | |
| Индекс воспламеняемости провода свечения | | | | IEC 60695-2-12 |
| 0.750 mm | 725 | -- | °C | |
| 1.50 mm | 750 | -- | °C | |
| 3.00 mm | 700 | -- | °C | |
| Температура зажигания провода свечения | | | | IEC 60695-2-13 |
| 0.750 mm | 750 | -- | °C | |
| 1.50 mm | 775 | -- | °C | |
| 3.00 mm | 725 | -- | °C | |
| Дополнительная информация | Сухой | Состояние | | Метод испытания |
|---|
| Automotive Materials -
(thickness d = 1 mm) | + | -- | | FMVSS 302 |
| Инъекция | Сухой | Единица измерения | |
|---|
| Температура сушки | 80.0 | °C | |
| Время сушки | 4.0 | hr | |
| Рекомендуемый Макс измельчения | 25 | % | |
| Задняя температура | 280 to 310 | °C | |
| Средняя температура | 280 to 310 | °C | |
| Передняя температура | 280 to 310 | °C | |
| Температура сопла | 280 to 310 | °C | |
| Температура обработки (расплава) | 285 to 305 | °C | |
| Температура формы | 65.0 to 95.0 | °C | |