Описание материалов:
Menzolit® SMC 1000 is a sheet moulding compound based on unsaturated polyester resin. The product is glass fibre reinforced and contains mineral fillers. In case of fire the product doesn't melt, neither does it form droplets nor is smoke generation excessive. The material is compression moulded in heated steel moulds. It is recommended to work with chrome plated tools. The product contains no halogens.
Menzolit® SMC 1000 is a special SMC for hydrolysis resistant applications. The glass level has been selected to combine good mouldability with good strength and stiffness properties. Typical applications are components facing exposure to water or moisture. This may be housings, covers and similar components exposed to a tropical climat or humid plant environment causing extensive immersion in water or exposure to high humidity. Sectional watertank panels are another very typical application.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Стекло \ Mineral, 25% наполнитель по весу
|
| Характеристики | - Огнестойкий
- Хорошая плавность
- Хорошая жесткость
- Хорошая прочность
- Без галогенов
- Высокая термостойкость
- Устойчивость к гидролизу
- Низкий уровень дыма
|
| Используется | |
| Внешний вид | |
| Формы | - Smc-лист формовочный состав
|
| Метод обработки | |
| Код маркировки деталей (ISO 11469) | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 1.70 | g/cm³ | ISO 1183 |
| Формовочная усадка | | | |
| -- 1 | 0.0 | % | DIN 53464 |
| -- | 0.080 | % | ISO 2577 |
| Поглощение воды (Saturation, 23°C) | < 0.30 | % | ISO 62 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения (Compression Molded) | 11000 | MPa | ISO 527-2 |
| Tensile Stress (Yield, Compression Molded) | 60.0 | MPa | ISO 527-2 |
| Флекторный модуль (Compression Molded) | 8000 | MPa | ISO 178 |
| Флекторный стресс (Compression Molded) | 145 | MPa | ISO 178 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность (Compression Molded) | 65 | kJ/m² | ISO 179 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | > 200 | °C | ISO 75-2/A |
| Температура непрерывного использования | 150 | °C | Internal Method |
| Температура перехода стекла | 145 | °C | DSC |
| CLTE-
Поток | 1.2E-5 | cm/cm/°C | ISO 11359-2 |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельное сопротивление поверхности | 1.0E+12 | ohms | IEC 60093 |
| Сопротивление громкости | 1.0E+15 | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 600 | V | IEC 60112 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Огнестойкость (3.00 mm) | HB | | UL 94 |
| Температура зажигания провода свечения | 850 | °C | IEC 60695-2-13 |
| Индекс кислорода | 28 | % | ISO 4589-2 |
| Дополнительная информация | Номинальное значение | | Метод испытания |
|---|
| Glow Bar | Level BH 2 <= 30 | | IEC 60707-3 |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура формы | 135 to 150 | °C | |
| Давление впрыска | 8.00 to 10.0 | MPa | |
| Примечание |
|---|
| 1 . | Post Molding Shrinkage |