Baytec MS-041 is a modified diphenylmethane diisocyanate (MDI)-terminated polyester prepolymer used in the manufacture of high-property solid cast polyurethane elastomers. The excellent resilience and low compression-set properties have enabled this material to be used for low-durometer printing rolls and squeegee blades. As with any product, use of Baytec MS-041 prepolymer in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.
| Главная Информация | |
|---|
| Характеристики | - Низкая деформация сжатия
- Гибкий
|
| Используется | |
| Формы | |
| Твердость | Номинальное значение | | Метод испытания |
|---|
| Твердость дюрометра (Shore A) | 72 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Устойчивость к истиранию (1000 Cycles, 1000 g, H-18 Wheel) | 10.0 | mg | ASTM D4066 |
| Отклонение сжатия | | | ASTM D575 |
| 10% | 1.00 | MPa | ASTM D575 |
| 15% | 1.59 | MPa | ASTM D575 |
| 2% | 0.172 | MPa | ASTM D575 |
| 20% | 2.17 | MPa | ASTM D575 |
| 25% | 2.83 | MPa | ASTM D575 |
| 5% | 0.483 | MPa | ASTM D575 |
| 50% | 8.10 | MPa | ASTM D575 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ASTM D412 |
| 100% strain | 3.17 | MPa | ASTM D412 |
| 200% strain | 4.27 | MPa | ASTM D412 |
| 300% strain | 5.65 | MPa | ASTM D412 |
| Прочность на растяжение (Break) | 35.2 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 560 | % | ASTM D412 |
| Tear Strength | | | |
| -- 1 | 56.9 | kN/m | ASTM D624 |
| Cracking | 18 | kN/m | ASTM D1938 |
| Комплект сжатия (70°C, 22 hr) | 20 | % | ASTM D395 |
| Сопротивляемость Bayshore | 52 | % | ASTM D2632 |
| Дополнительная информация |
|---|
| Appearance: Amber liquidNCO: 4.40 to 4.60 wt%Viscosity at 80°C: 4200 mPa-sViscosity at 100°C: 1100 mPa-sSpecific Gravity at 80°C: 1.18Specific Gravity at 100°C: 1.17Flash Point, PMCC: >93°CNCO/OH Ratio: 1.05Stoichiometry: 95% TheoryPrepolymer Temperature: 90 to 100°CExtender Temperature: 50 to 70°CMold Temperature: 100 to 110°CPot Life: 10 to 15 minDemold: >60 min |
| Тип материала |
Категория |
Производитель |
|
Xuchuan XCS-150P |
PUR, Unspecified |
Xuchuan Chemical (Suzhou) Co., Ltd
|
|
Xuchuan XCD-675A |
PUR, Unspecified |
Xuchuan Chemical (Suzhou) Co., Ltd
|
|
Xuchuan XCD-465 |
PUR, Unspecified |
Xuchuan Chemical (Suzhou) Co., Ltd
|
|
Epoxies, Ect. 50-2366 FR |
PUR, Unspecified |
Epoxies, Etc.
|
|
Huafon JF-D-NS2920 |
PUR, Unspecified |
Huafon Group Co., Ltd.
|
|
Andur 900-AP |
PUR-Est/eth,TDI |
Anderson Development Company
|