POLYTROPE® STR 1042EU-01 NATURAL
Описание материалов:
POLYTROPE STR 1042EU resin is a high melt strength thermoformable TPO that balances impact resistance and high stiffness, enabling processors and end users to reduce product weight and improve processing efficiency without sacrificing product performance. The attractive performance features of POLYTROPE STR 1042EU resin uniquely positions it as a economically favorable option to traditional engineered resins. It can be extruded in smooth or textured surfaces, or co-extruded with a POLYTROPE STR enhanced polyolefin cap resin to further customize its' durability, appearance, or feel for interior and exterior applications. The capability of POLYTROPE STR 1042EU to provide an exceptionally smooth surface in extrusion and thermoforming makes it well suited to lamination processes with decorative films. It is also easily colored and is paintable by standard TPO paint systems.
| Главная Информация | |
|---|
| Характеристики | - Низкий CLTE
- Перерабатываемые материалы
- Распылитель
- Хорошая прочность расплава
- Ударопрочность при низкой температуре
- Хорошая устойчивость к погоде
|
| Формы | |
| Метод обработки | - Коэкструзионное формование
- Экструзия
- Экструзионный лист
- Термоформовка
- Экструзионное формование профиля
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес 1 | 1.16 | g/cm³ | ISO 1183 |
| Массовый расход расплава (MFR) (230°C/2.16 kg) | 0.50 | g/10 min | ISO 1133 |
| Формовочная усадка (23°C, 24 hr, 3.18 mm) | 0.70 - 0.90 | % | ISO 294-4 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение | | | |
| Yield | 22.9 | MPa | ASTM D638 |
| Yield, 23°C 2 | 23.6 | MPa | ISO 527-2 |
| Растяжимое напряжение 3(Break, 233°C) | > 200 | % | ISO 527-2 |
| Флекторный модуль-
Аккорд 4(23°C) | 2510 | MPa | ISO 178 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Ударная прочность | | | ISO 179 |
| -30°C | 4.1 | kJ/m² | ISO 179 |
| 23°C | 62 | kJ/m² | ISO 179 |
| Зубчатый изод Impact | | | |
| -30°C | 53 | J/m | ASTM D256 |
| 23°C | 860 | J/m | ASTM D256 |
| -30°C | 4.7 | kJ/m² | ISO 180 |
| 23°C | 54 | kJ/m² | ISO 180 |
| Ударное устройство для дротиков (-30°C, Total Energy, Ductile Failure) | 48.6 | J | ASTM D3763 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Heat Deflection Temperature | | | |
| 0.45 MPa, not annealed | 114 | °C | ISO 75-2/Bf |
| 1.8 MPa, not annealed | 60.2 | °C | ISO 75-2/A |
| Линейный коэффициент теплового расширения | | | ASTM E831 |
| Flow
: -30 to 100°C | 4.5E-5 | cm/cm/°C | ASTM E831 |
| Lateral | 1.3E-4 | cm/cm/°C | ASTM E831 |
| Воспламеняемость | Номинальное значение | | Метод испытания |
|---|
| Огнестойкость (3.2 mm, All Colors) | HB | | UL 94 |
| Оптический | Номинальное значение | | Метод испытания |
|---|
| Блестящий Гарднер (60°, 3180 µm, Thermoformed, Smooth) | 20 - 40 | | ISO 2813 |
| Примечание |
|---|
| 1 . | Method A |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1A, 2.0 mm/min |