LUVOCOM® 20-8943

Категория	PPA, Polyphthalamide
Производитель	Lehmann & Voss & Co.
Торговая марка	LUVOCOM®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	gDdXB7_LUVOCOM-20-8943.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOCOM®20-8943 is a polyxylylamide (PPA) material containing a mineral filler. This product is available in Europe,.

LUVOCOM®The main features of 20-8943 are:

anti-warping

Good stiffness

Typical application areas include:

engineering/industrial accessories

textile/fiber

Automotive Industry

business/office supplies

Главная Информация
Наполнитель/армирование	Минеральный наполнитель
Характеристики	Низкий уровень защиты Жесткий, хороший Хорошая прочность
Используется	Детали Насоса Втулка Шестерня Текстильные изделия Инженерные аксессуары Применение в автомобильной области Бизнес-оборудование Подшипник
Внешний вид	Натуральный цвет

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.51	g/cm³	ISO 1183
Формовочная усадка	0.40 - 0.70	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 0.30	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	14000	MPa	ISO 527-2
Tensile Stress (Break)	105	MPa	ISO 527-2
Растяжимое напряжение (Yield)	1.5	%	ISO 527-2
Флекторный модуль	12000	MPa	ISO 178
Флекторный стресс	160	MPa	ISO 178
Flexural Strain at Flexural Strength	2.0	%	ISO 178

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Максимальная рабочая температура- Короткий срок	195	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Charpy Unnotched Impact Strength (23°C)	13	kJ/m²	ISO 179/1eU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Температура непрерывного использования	165	°C	UL 746B

Электрический	Номинальное значение	Единица измерения	Метод испытания
Удельное сопротивление поверхности	> 1.0E+12	ohms	IEC 60093

Инъекция	Номинальное значение	Единица измерения
Температура сушки
A	80.0	°C
B	110	°C
Время сушки
A	6.0 - 16	hr
B	4.0 - 6.0	hr
Рекомендуемая максимальная влажность	0.050	%
Задняя температура	320 - 340	°C
Средняя температура	320 - 340	°C
Передняя температура	320 - 345	°C
Температура сопла	330 - 345	°C
Температура обработки (расплава)	340	°C
Температура формы	110 - 150	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.05%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Processing temperatures above 340°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.05%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Processing temperatures above 340°C may very rapidly cause thermal damage and should therefore be avoided. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Тип материала	Категория	Производитель
HiFill® PPA GF35 IM AHWR	PPA	Techmer Engineered Solutions
VESTAMID® HTplus M1036	PPA	Evonik Industries AG
DynaMix™ 4100-28CF	PPA	Polymer Dynamix
RTP 4002 TFE 10	PPA	RTP Company
RTP 4002 TFE 15	PPA	RTP Company
RTP 4000 TFE 10	PPA	RTP Company

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

