Описание материалов:
Baytec MS-092 is a modified diphenylmethane diisocyanate (MDI)-terminated polyester prepolymer. It is used in the manufacture of high-property solid cast polyurethane elastomers. As with any product, use of Baytec MS-092 prepolymer in a given application must be tested (including field testing, etc.) in advance by the user to determine suitability.
| Твердость | Номинальное значение | | Метод испытания |
|---|
| Твердость дюрометра (Shore D) | 50 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Устойчивость к истиранию (1000 Cycles, 1000 g, H-18 Wheel) | 42.0 | mg | ASTM D3498 |
| Отклонение сжатия | | | ASTM D575 |
| 10% | 4.83 | MPa | ASTM D575 |
| 15% | 8.96 | MPa | ASTM D575 |
| 2% | 0.827 | MPa | ASTM D575 |
| 20% | 22.8 | MPa | ASTM D575 |
| 25% | 33.1 | MPa | ASTM D575 |
| 5% | 3.45 | MPa | ASTM D575 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress | | | ASTM D412 |
| 100% strain | 13.1 | MPa | ASTM D412 |
| 200% strain | 15.5 | MPa | ASTM D412 |
| 300% strain | 19.3 | MPa | ASTM D412 |
| Прочность на растяжение (Break) | 42.1 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 480 | % | ASTM D412 |
| Tear Strength | | | |
| -- 1 | 118 | kN/m | ASTM D624 |
| Cracking | 66 | kN/m | ASTM D1938 |
| Комплект сжатия (70°C, 22 hr) | 26 | % | ASTM D395 |
| Сопротивляемость Bayshore | 42 | % | ASTM D2632 |
| Дополнительная информация |
|---|
| Appearance: Pale yellow liquidNCO: 8.95 to 9.34 wt%Flash Point, PMCC: 222°CSpecific Gravity at 80°C: 1.15Specific Gravity at 100°C: 1.13Viscosity at 80°C: 750 mPa-sViscosity at 100°C: 365 mPa-sNCO/OH Ratio: 1.10Stoichiometry: 90% TheoryPrepolymer Temperature: 90 to 100°CExtender Temperature: 100 to 110°CMold Temperature: 100 to 110°CPot Life: 2 to 4 minDemold: 30 min |