Geon™ Specialty Suspension Atlas S140
Описание материалов:
Geon® Atlas S140 is high molecular weight homopolymer specialty suspension resin intended for use in high strength extruded parts. It improves the physical performance of end application for intsance wire and cable insulation, extruded tubes. The high porosity property of this resin allows rapid plasticizer absorption reducing the compound cycle times and resulting in high compound throughput and low manufacturing cost. Geon® Atlas S140 improves heat distortion (HDT) performance, increase the strength for highly plasticized formulas, and provides longer product shelf life.
| Главная Информация | |
|---|
| Характеристики | |
| Используется | - Применение проводов и кабелей
- Изоляционный материал
|
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.40 | g/cm³ | ASTM D792 |
| K-Value 1 | 82.0 | | Internal method |
| Загрязнения | | | Internal method |
| Dark Particles 2 | 1 | | Internal method |
| Light Colored Particles 3 | 4 | | Internal method |
| Magnetic Particles 4 | 0 | | Internal method |
| Видимая свободная плотность 5 | 0.410 | g/cm³ | Internal method |
| Внутренняя вязкость 6 | 1.4 | | ASTM D1243-60-A |
| Размер частиц | | | Internal method |
| <105 micron 7 | 14.8 | % | Internal method |
| > 250 micron 8 | 3.40 | % | Internal method |
| Average Particle Size 9 | 145 | µm | Internal method |
| Relative Viscosity 10 | 3.10 | | Internal method |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Оптимальное растяжение 11 | 17.9 | MPa | ASTM D638 |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Время смешивания порошка 12 | 2.6 | min | Internal method |
| Остаточный винилхлорид мономер 13 | | ppm | Internal method |
| Испарители 14 | 0.070 | % | Internal method |
| Процесс полимеризации | Suspension | | |
| Пористость 15 | 0.570 | cm³/g | Internal method |
| Время потока-
Условное время потока воронки 16 | 27.0 | sec | Internal method |
| Note:The value set forth represent 'typical' values and Mexichem Specialty Resins, therefore, makes no representation that the material in any particular shipment will conform to the listed properties.Packaging: This resin is shipped in multi-wall paper bags, netweight 50lbs, 2,500lbs per pallet. Information shown on the package includes commercial identification number, lot, and weight.STP 488 (formulation): 100phr Geon® Atlas S140, 55phr TOTM, and 18phr FillerASTM D638 (formulation): 100phr Geon® Atlas S140, 60phr DINP, 5phr ESO, and 2phr Mark 4716 |
| Примечание |
|---|
| 1 . | Interrelationship |
| 2 . | Geon® 1217 |
| 3 . | Geon® 1005 |
| 4 . | Geon® STP 1217Unit: #/100in2 |
| 5 . | Geon® STP 1169 |
| 6 . | Puli 1386 |
| 7 . | Through the 140 net, Geon®812 |
| 8 . | Keep at 40 60 nets, Geon®812 |
| 9 . | Geon® DFT 1466 |
| 10 . | Interrelationship |
| 11 . | With provided formulation |
| 12 . | Geon® STP 488 with provided formulation |
| 13 . | Geon® STP 1005 |
| 14 . | Bags, Geon®793 |
| 15 . | Geon® 1094 |
| 16 . | Geon® STP 1169 |