Описание материалов:
LLGF-123D is a certified prime grade Ethylene-Octene Copolymer specially developed for production of High Performance Blown films of outstanding mechanical properties, LLGF-123D features easy processability and films exhibit high toughness, very good Elmendorf Tear, high Impact strength and Puncture resistance. LLGF-123D major applications include film coextrusion, super strength liners, lamination films, stretch wrapping films, food packaging, and superior load retention carry-on-bags. Maximum recommended film drawdown is 0.4 mil. LLGF-123D contains medium slip and high antiblock. LLGF-123D complies with FDA regulation 21CFR 177.1520 (c) 3.2(a) and most international regulations concerning the use of Polyethylene in contact with food articles.
| Главная Информация | |
|---|
| Добавка | - Высокая устойчивость к царапинам
- Умеренная гладкость
|
| Характеристики | - Высокая устойчивость к царапинам
- Высокая прочность
- Сополимер
- Сопротивление перфорации
- Высокая ударопрочность
- Обрабатываемость, хорошая
- Хорошая прочность на разрыв
- Хорошая прочность
- Соответствие пищевого контакта
- Октеновый комномер
- Умеренная гладкость
|
| Используется | - Упаковка
- Пленка
- Ламинат
- Подкладка
- Сумка
- Растягивающаяся обмотка
- Пищевая упаковка
|
| Рейтинг агентства | - FDA 21 CFR 177,1520 (c) 3.2a
|
| Формы | |
| Метод обработки | - Выдувная пленка
- Коэкструзионное формование
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.923 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 25 | µm | |
| Сектантный модуль | | | ASTM D882 |
| 1% secant, MD
: 25 µm | 186 | MPa | ASTM D882 |
| 1% secant, TD
: 25 µm | 207 | MPa | ASTM D882 |
| Прочность на растяжение | | | ASTM D882 |
| MD
: Yield, 25 µm | 10.0 | MPa | ASTM D882 |
| TD
: Yield, 25 µm | 10.0 | MPa | ASTM D882 |
| MD
: Break, 25 µm | 48.0 | MPa | ASTM D882 |
| TD
: Break, 25 µm | 44.0 | MPa | ASTM D882 |
| Удлинение при растяжении | | | ASTM D882 |
| MD
: Break, 25 µm | 440 | % | ASTM D882 |
| TD
: Break, 25 µm | 770 | % | ASTM D882 |
| Ударное падение Dart 1(25 µm) | 330 | g | ASTM D1709A |
| Elmendorf Tear Strength | | | ASTM D1922 |
| MD
: 25 µm | 400 | g | ASTM D1922 |
| TD
: 25 µm | 730 | g | ASTM D1922 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блеск (45°, 25.0 µm, Blown Film) | 45 | | ASTM D2457 |
| Haze (25.0 µm, Blown Film) | 14 | % | ASTM D1003 |
| Дополнительная информация |
|---|
| Film Specimen: 1.0 mil (25 µm) film, melt temperature 420-450°F (215-230°C), blow-up-ratio 2.5 :1. |