LUVOCOM® 1106-8892

Категория	PEI, Polyether Imide
Производитель	LEHVOSS Group
Торговая марка	LUVOCOM®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	evwf5D_LUVOCOM11068892.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOCOM®1106-8892 is a polyetherimide (PEI) material, and the filler is glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 1106-8892 are:

Flame Retardant

Good stiffness

Главная Информация
Наполнитель/армирование	Армированный стекловолокном материал
Характеристики	Жесткий, хороший Хорошая прочность Огнестойкий
Внешний вид	Черный

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.42	g/cm³	ISO 1183
Формовочная усадка	0.20 - 0.50	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 0.30	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	8500	MPa	ISO 527-2
Tensile Stress (Break)	155	MPa	ISO 527-2
Растяжимое напряжение (Yield)	2.5	%	ISO 527-2
Флекторный модуль	7000	MPa	ISO 178
Флекторный стресс	220	MPa	ISO 178
Flexural Strain at Flexural Strength	3.3	%	ISO 178

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Максимальная рабочая температура- Короткий срок	200	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance	> 1.0E+12	ohms	IEC 60167

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Charpy Unnotched Impact Strength (23°C)	40	kJ/m²	ISO 179/1eU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Heat Deflection Temperature (1.8 MPa, Unannealed)	205	°C	ISO 75-2/A
Температура непрерывного использования	170	°C	UL 746B
Викат Температура размягчения	220	°C	ISO 306/A

Электрический	Номинальное значение	Единица измерения	Метод испытания
Удельное сопротивление поверхности	> 1.0E+12	ohms	IEC 60093

Инъекция	Номинальное значение	Единица измерения
Температура сушки
Hot air dryer, A	120	°C
Hot air dryer, B	150	°C
Время сушки
Hot air dryer, A	> 8.0	hr
Hot air dryer, B	> 4.0	hr
Задняя температура	330 - 350	°C
Средняя температура	340 - 390	°C
Передняя температура	350 - 400	°C
Температура сопла	350 - 400	°C
Температура обработки (расплава)	380	°C
Температура формы	150 - 180	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.03%, otherwise porosity and surface defects (e.g. smearing) may occur. Predrying is recommended even when sealed original containers are being used. To avoid internal stresses, a low shear load should be used for processing. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.03%, otherwise porosity and surface defects (e.g. smearing) may occur. Predrying is recommended even when sealed original containers are being used. To avoid internal stresses, a low shear load should be used for processing. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.

Тип материала	Категория	Производитель
ULTEM™ LTX300A resin	PEI	SABIC Innovative Plastics
Complet® LGF40-PEI	PEI	PlastiComp, Inc.
RTP 2101 Z	PEI	RTP Company
RTP 2100 TFE 5	PEI	RTP Company
ULTEM™ 2210F resin	PEI	SABIC Innovative Plastics Europe
LNP™ THERMOCOMP™ EX06430H compound	PEI	SABIC Innovative Plastics

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

