LUVOCOM® 6-8618

Категория	PA12, Polyamide 12 , Nylon 12
Производитель	Lehmann & Voss & Co.
Торговая марка	LUVOCOM®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	eozcTw_LUVOCOM-6-8618.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOCOM®6-8618 is a polyamide 12 (nylon 12) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 6-8618 are:

Conductivity

Electrostatic protection

moisture resistance

Typical application areas include:

textile/fiber

engineering/industrial accessories

Automotive Industry

business/office supplies

Главная Информация
Характеристики	Проводящий Теплопроводность Защита от электростатического разряда Низкий или не впитывающий
Используется	Текстильные изделия Инженерные аксессуары Применение в автомобильной области Бизнес-оборудование
Внешний вид	Серый

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.15	g/cm³	ISO 1183
Формовочная усадка	0.50 - 0.90	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 0.10	%

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	4500	MPa	ISO 527-2
Tensile Stress (Break)	75.0	MPa	ISO 527-2
Растяжимое напряжение (Yield)	4.7	%	ISO 527-2
Флекторный модуль	4000	MPa	ISO 178
Флекторный стресс	95.0	MPa	ISO 178
Flexural Strain at Flexural Strength	5.5	%	ISO 178

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Максимальная рабочая температура- Короткий срок	140	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance		ohms	IEC 60167

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Charpy Unnotched Impact Strength (23°C)	25	kJ/m²	ISO 179/1eU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Температура непрерывного использования	90.0	°C	UL 746B
Теплопроводность ¹	9.5	W/m/K

Электрический	Номинальное значение	Единица измерения	Метод испытания
Удельное сопротивление поверхности	< 1.0E+7	ohms	IEC 60093

Инъекция	Номинальное значение	Единица измерения
Температура сушки
A	75.0	°C
B	105	°C
Время сушки- A	6.0 - 10	hr
Рекомендуемая максимальная влажность	0.10	%
Задняя температура	230 - 250	°C
Средняя температура	240 - 260	°C
Передняя температура	250 - 270	°C
Температура сопла	250 - 260	°C
Температура обработки (расплава)	250	°C
Температура формы	70.0 - 110	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Примечание
1 .	Hot-Disk, 60x60x3 mm

Тип материала	Категория	Производитель
ExTima™ GP MB PA12 720	Nylon 12	Ovation Polymers Inc.
NYCOA Polyamide 7551 T	Nylon 12	Nycoa (Nylon Corporation of America)
Latistat 83-05	Nylon 12	LATI S.p.A.
RTP 206F	Nylon 12	RTP Company
VESTAMID® E E40-S3	Nylon 12	Evonik Industries AG
HiFill® PA12 GF30 L	Nylon 12	Techmer Engineered Solutions