LUVOCOM® 1301-8456

Категория PPS, Polyphenylene Sulfide
Производитель Lehmann & Voss & Co.
Торговая марка LUVOCOM®
Порт Китай Шанхайский порт
Торговые условия FOB, CFR, CIF
Платежное средство L/C, T/T, Western Union
PDF eif5FY_LUVOCOM-1301-8456.pdf
Контактная информация
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Описание материалов:
LUVOCOM®1301-8456 is a linear polyphenylene sulfide material, and the filler is glass fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 1301-8456 are:
  • flame retardant/rated flame
  • Flame Retardant
  • High stiffness
  • high strength
  • Creep resistance

Typical application areas include:
  • engineering/industrial accessories
  • textile/fiber
  • Automotive Industry
  • business/office supplies
  • medical/health care
Главная Информация
Наполнитель/армирование
  • Армированный стекловолокном материал
Добавка
  • Ptfe лубрикант
Характеристики
  • Низкий коэффициент трения
  • Жесткий, высокий
  • Высокая прочность
  • Хорошее сопротивление ползучести
  • Хорошая химическая стойкость
  • Хорошая стойкость к истиранию
  • Теплостойкость, высокая
  • Смазка
  • Огнестойкий
Используется
  • Детали Насоса
  • Шестерня
  • Текстильные изделия
  • Инженерные аксессуары
  • Применение в автомобильной области
  • Бизнес-оборудование
  • Медицинские принадлежности/принадлежности для ухода
Внешний вид
  • Черный
ФизическийНоминальное значениеЕдиница измеренияМетод испытания
Плотность 1.68g/cm³ISO 1183
Формовочная усадка 0.20 - 0.40%DIN 16901
Поглощение воды (23°C, 24 hr)< 0.050%
МеханическиеНоминальное значениеЕдиница измеренияМетод испытания
Модуль растяжения 13000MPaISO 527-2
Tensile Stress (Break)130MPaISO 527-2
Растяжимое напряжение (Yield)1.7%ISO 527-2
Флекторный модуль 11000MPaISO 178
Флекторный стресс 200MPaISO 178
Коэффициент трения
    Dynamic 0.20
    Static 0.15
Flexural Strain at Flexural Strength 2.2%ISO 178
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Максимальная рабочая температура- Короткий срок 240°C
ЭлектрическийНоминальное значениеЕдиница измеренияМетод испытания
Insulation Resistance > 1.0E+12ohmsIEC 60167
ВоздействиеНоминальное значениеЕдиница измеренияМетод испытания
Charpy Unnotched Impact Strength (23°C)35kJ/m²ISO 179/1eU
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Heat Deflection Temperature (1.8 MPa, Unannealed)250°CISO 75-2/A
Температура непрерывного использования 220°CUL 746B
Викат Температура размягчения 240°CISO 306/A
ВоспламеняемостьНоминальное значениеЕдиница измеренияМетод испытания
Огнестойкость 1V-0UL 94
ИнъекцияНоминальное значениеЕдиница измерения
Температура сушки
    B 50.0 - 90.0°C
    Hot air dryer, A 100 - 140°C
Время сушки
    B > 4.0hr
    Hot air dryer, A 2.0 - 4.0hr
Задняя температура 300 - 320°C
Средняя температура 310 - 330°C
Передняя температура 320 - 340°C
Температура сопла 320 - 340°C
Температура обработки (расплава) 330°C
Температура формы 150 - 180°C
Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information The material does not necessarily have to be predried; when originally sealed containers are used, this process may normally be omitted. Processing temperatures above 360°C may very rapidly cause thermal damage and should therefore be avoided. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.
Примечание
1 .Not recognized by UL.
Тип материала Категория Производитель
DynaPath™ C3850CF PPS Polymer Dynamix
Lion Idemitsu Composites PPS G131J1 PPS Lion Idemitsu Composites Co., Ltd.
LUVOCOM® 1301-8066 VP PPS, Linear Lehmann & Voss & Co.
RTP 1383 P-1 TFE 15 PPS RTP Company
RTP 1385 HM PPS RTP Company
LNP™ LUBRICOMP™ OCP36 compound PPS SABIC Innovative Plastics
Получите информацию об этом продукте следующим способом.
Телефон+086 13424755533
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Copyright © russianpolymer.com All Rights Reserved
Получите информацию об этом продукте следующим способом.
+08613424755533
sales@su-jiao.com

Служба поддержки клиентов Вичат
Свяжитесь с нами