TOTAL Polyethylene Lumicene® M 6040
Описание материалов:
Lumicene® mPE M 6040 is a second generation metallocene high density Polyethylene.
Lumicene® mPE M 6040 can be processed at high output rates with low extrusion pressure, low neck-in, excellent drawability and gauge control in comparison with conventional LLDPE and first generation metallocene based polyethylene. The high stiffness combined with good optical properties brings a significant down-gauging potential.
Lumicene® mPE M 6040 is a versatile resin that can be used in pure or in blend for the production of both monolayer and multilayer film. Typical applications are: specialty film, hygiene film, embossed film, compounds and consumer and automatic packaging, such as produce bags, mailing and hygiene overwrap film. The high density of Lumicene® mPE M 6040 enables its use in applications with moisture barrier requirements, such as dry food packaging, and brings improved heat resistance, compared to commonly used HDPE.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Жесткий, высокий
- Оптическая производительность
- Устойчивость к окислению
- Обрабатываемость, хорошая
- Низкая внутренняя усадка
|
| Используется | - Упаковка
- Пленка
- Сумка
- Многослойная пленка
- Смешивание
- Пищевая упаковка
|
| Рейтинг агентства | |
| Метод обработки | - Экструзионная пленка
- Литая пленка
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.960 | g/cm³ | ISO 1183 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 4.0 | g/10 min | ISO 1133 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 20 | µm | |
| Tensile Stress | | | ISO 527-3 |
| MD
: Yield, 20 µm, cast film | 23.0 | MPa | ISO 527-3 |
| TD
: Yield, 20 µm, cast film | 24.0 | MPa | ISO 527-3 |
| MD
: Fracture, 20 µm, cast film | 26.0 | MPa | ISO 527-3 |
| TD
: Fracture, 20 µm, cast film | 34.0 | MPa | ISO 527-3 |
| Удлинение при растяжении | | | ISO 527-3 |
| MD
: Fracture, 20 µm, cast film | 520 | % | ISO 527-3 |
| TD
: Fracture, 20 µm, cast film | 850 | % | ISO 527-3 |
| Ударное падение Dart (20 µm, Cast Film) | 40 | g | ISO 7765-1 |
| Elmendorf Tear Strength 1 | | | ISO 6383-2 |
| MD
: 20.0 µm | 8.0 | kN/m | ISO 6383-2 |
| TD
: 20.0 µm | 70.0 | kN/m | ISO 6383-2 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Викат Температура размягчения | 132 | °C | ISO 306 |
| Температура плавления | 134 | °C | ISO 11357-3 |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Блеск (45°, 20.0 µm, Cast Film) | 51 | | ASTM D2457 |
| Haze (20.0 µm, Cast Film) | 12 | % | ISO 14782 |
| Дополнительная информация |
|---|
| Laboratory test specimens produced at the following extrusion conditions: die gap = 250 µm, chill roll temperature = 20°C, throughput = 7 kg/h, melt temperature = 260 °C |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | 220 - 280 | °C | |
| Рулон для снятия | 20.0 - 80.0 | °C | |