Описание материалов:
Applications:
PETROTHENE NA963 is a series of resins formulated with special antiblock additive and designed for a wide variety of industrial film applications where high impact strength and excellent drawdown are needed. NA963 exhibits uniformity, ease of processing and good tensile strength.
Regulatory Status:
The basic resin NA963 meets the requirements of the Food and Drug Administration, 21 CFR 177.1520. This regulation allows the use of this olefin polymer in "...articles or components of articles intended for use in contact with food." Specific limitations or conditions of use may apply. Contact your Equistar sales representative for further information regarding the suitability of specific products for specific applications.
| Главная Информация | |
|---|
| Характеристики | - Высокая ударопрочность
- Обрабатываемость, хорошая
- Хорошее Отшелушивание
- Хорошая прочность
- Соответствие пищевого контакта
|
| Используется | - Пленка
- Промышленное применение
|
| Рейтинг агентства | - Управление по санитарному надзору за качеством пищевых продуктов и медикаментов 21 CFR 177,1520
|
| Формы | |
| Метод обработки | - Экструзионная пленка
- Выдувная пленка
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.919 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.70 | g/10 min | ASTM D1238 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore D) | 46 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение | | | ASTM D638 |
| Yield | 10.7 | MPa | ASTM D638 |
| Fracture | 11.4 | MPa | ASTM D638 |
| Удлинение при растяжении | | | ASTM D638 |
| Yield | 100 | % | ASTM D638 |
| Fracture | 700 | % | ASTM D638 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Толщина пленки протестирована | 32 | µm | |
| Сектантный модуль | | | ASTM D882 |
| 1% secant, MD
: 32 µm | 179 | MPa | ASTM D882 |
| 1% secant, TD
: 32 µm | 221 | MPa | ASTM D882 |
| Прочность на растяжение | | | ASTM D882 |
| MD
: Yield, 32 µm | 23.4 | MPa | ASTM D882 |
| TD
: Yield, 32 µm | 16.5 | MPa | ASTM D882 |
| Удлинение при растяжении | | | ASTM D882 |
| MD
: Broken, 32 µm | 160 | % | ASTM D882 |
| TD
: Broken, 32 µm | 480 | % | ASTM D882 |
| Ударное падение Dart (32 µm) | 130 | g | ASTM D1709 |
| Elmendorf Tear Strength | | | ASTM D1922 |
| MD
: 32 µm | 300 | g | ASTM D1922 |
| TD
: 32 µm | 180 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура ломкости | -75.0 | °C | ASTM D746 |
| Викат Температура размягчения | 90.0 | °C | ASTM D1525 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура расплава | 154 - 177 | °C | |
| Инструкции по экструзии |
|---|
| Generally recommended extrusion conditions include a melt temperature range of 310°-350°F (155°-177°C) and a blow-up ratio range of 1.8-2.5:1. Drawdown to gauges below 1.0 mils (<25 microns) is possible at commercial rates when proper techniques are used. |