UmaPET WHHSO
| Категория | PET, Polyethylene Terephthalate |
| Производитель | Ester Industries Ltd. |
| Торговая марка | UmaPET |
| Порт | Китай Шанхайский порт |
| Торговые условия | FOB, CFR, CIF |
| Платежное средство | L/C, T/T, Western Union |
dbvZOr_UmaPET-WHHSO.pdf  |
|
| Контактная информация |  Служба поддержки клиентов Вичат |
|
|
|
Описание материалов:
KEY FEATURES
APPLICATIONS
- Uma PET WHHS is white opaque film with one side sealable layer with itself along with APET,C-PET, modified C-PET and A-PET coated boards.
- The film has high opacity and high whiteness index along with low transparency.
- Excellent flatness and good dimensional stability at elevated temperatures and exhibits good processability.
APPLICATIONS
- Design for lidding in packaging applications and other industrial applications.
- Users don't need to coat any sealable coating during conversion.
| Главная Информация | |
|---|---|
| Характеристики |
|
| Используется |
|
| Внешний вид |
|
| Формы |
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Формовочная усадка | ASTM D1204 | ||
| Flow : 150°C, 30 min, 0.0300 mm | 2.5 | % | |
| Flow : 150°C, 30 min, 0.0360 mm | 2.5 | % | |
| Flow : 150°C, 30 min, 0.0500 mm | 2.0 | % | |
| Across Flow : 150°C, 30 min, 2.30E-5 mm | 0.60 | % | |
| Across Flow : 150°C, 30 min, 0.0300 mm | 0.60 | % | |
| Across Flow : 150°C, 30 min, 0.0360 mm | 0.60 | % |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Коэффициент трения | ASTM D1894 | ||
| vs. Itself - Dynamic 1 | 0.45 | ||
| vs. Itself - Dynamic 2 | 0.45 | ||
| vs. Itself - Dynamic 3 | 0.45 | ||
| vs. Itself - Static 4 | 0.55 | ||
| vs. Itself - Static 5 | 0.55 | ||
| vs. Itself - Static 6 | 0.55 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Толщина пленки протестирована | 30 36 50 | µm | |
| Толщина пленки-рекомендовано/доступно | 30, 36, 50 µm | ||
| Прочность на растяжение | ASTM D882 | ||
| MD : Break, 30 µm | 137 | MPa | |
| MD : Break, 36 µm | 137 | MPa | |
| MD : Break, 50 µm | 137 | MPa | |
| TD : Break, 30 µm | 147 | MPa | |
| TD : Break, 36 µm | 147 | MPa | |
| TD : Break, 50 µm | 147 | MPa | |
| Удлинение при растяжении | ASTM D882 | ||
| MD : Break, 30 µm | 130 | % | |
| MD : Break, 36 µm | 130 | % | |
| MD : Break, 50 µm | 130 | % | |
| TD : Break, 30 µm | 80 | % | |
| TD : Break, 36 µm | 80 | % | |
| TD : Break, 50 µm | 80 | % | |
| Выход | Internal Method | ||
| 30.0 µm | 23.8 | m²/kg | |
| 36.0 µm | 19.8 | m²/kg | |
| 50.0 µm | 14.1 | m²/kg |
| Дополнительная информация | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Прочность уплотнения 7 | Internal Method | ||
| 140°C, 30.0 µm | 984.3 | g/2.5 cm | |
| 140°C, 36.0 µm | 984.3 | g/2.5 cm | |
| 140°C, 50.0 µm | 984.3 | g/2.5 cm | |
| Смачивающее натяжение- Простая сторона | ASTM D2578 | ||
| 30.0 µm | 44 | dyne/cm | |
| 36.0 µm | 44 | dyne/cm | |
| 50.0 µm | 44 | dyne/cm |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|---|---|---|
| Непрозрачность | Internal Method | ||
| -- 8 | 85 | % | |
| -- 9 | 85 | % | |
| -- 10 | 85 | % | |
| Haze | ASTM D1003 | ||
| 30.0 µm | 98 | % | |
| 36.0 µm | 98 | % | |
| 50.0 µm | 98 | % |
| Примечание | |
|---|---|
| 1 . | 50 µm |
| 2 . | 36 µm |
| 3 . | 30 µm |
| 4 . | 30 µm |
| 5 . | 36 µm |
| 6 . | 50 µm |
| 7 . | Seal to seal surface, 2s, 3 kg/cm² pressure |
| 8 . | 50 µm |
| 9 . | 36 µm |
| 10 . | 30 µm |
| Тип материала | Категория | Производитель |
|---|---|---|
| Artenius DESIGN | PET | Artenius |
| SCHULADUR® E GF 35 | PET | A. Schulman Europe |
| TechnoPet 3520 | PET | TechnoCompound GmbH |
| KOPET® KP133G15GN | PET | Kolon Plastics, Inc. |
| Petra® 130 | PET | BASF Corporation |
| HiFill® PET GF/M40 BK | PET | Techmer Engineered Solutions |
Получите информацию об этом продукте следующим способом.
| Телефон | +086 13424755533 |
| EMAIL US | sales@su-jiao.com |
Служба поддержки клиентов Вичат | |
Copyright © russianpolymer.com All Rights Reserved