LUVOCOM® 65-8961/ES

Категория	PP, Polypropylene Copolymer , PP Copolymer
Производитель	LEHVOSS Group
Торговая марка	LUVOCOM®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	dPQFKl_LUVOCOM658961ES.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

LUVOCOM®65-8961/ES is a polypropylene copolymer (PP Copoly) material, which contains stainless steel fiber. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 65-8961/ES are:

Conductivity

Electromagnetic shielding (EMI)

Главная Информация
Наполнитель/армирование	Волокно из нержавеющей стали
Характеристики	Проводящий Электромагнитное Экранирование (EMI) Статическая проводимость
Внешний вид	Черный

Физический	Номинальное значение	Единица измерения	Метод испытания
Плотность	1.20	g/cm³	ISO 1183
Формовочная усадка	1.0 - 1.6	%	DIN 16901
Поглощение воды (23°C, 24 hr)	< 0.10	%

Твердость	Номинальное значение	Единица измерения	Метод испытания
Твердость дюрометра (Shore D)	74		ISO 868

Механические	Номинальное значение	Единица измерения	Метод испытания
Модуль растяжения	2500	MPa	ISO 527-2
Tensile Stress (Break)	33.0	MPa	ISO 527-2
Растяжимое напряжение (Yield)	4.9	%	ISO 527-2
Флекторный модуль	2000	MPa	ISO 178
Флекторный стресс	46.0	MPa	ISO 178
Flexural Strain at Flexural Strength	6.5	%	ISO 178

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Максимальная рабочая температура- Короткий срок	110	°C

Электрический	Номинальное значение	Единица измерения	Метод испытания
Insulation Resistance	1.0 - 3.2	ohms	IEC 60167

Воздействие	Номинальное значение	Единица измерения	Метод испытания
Charpy Unnotched Impact Strength
-30°C	27	kJ/m²	ISO 179/1fU
23°C	29	kJ/m²	ISO 179/1eU

Тепловой	Номинальное значение	Единица измерения	Метод испытания
Heat Deflection Temperature (1.8 MPa, Unannealed)	59.0	°C	ISO 75-2/A
Температура непрерывного использования	80.0	°C	UL 746B
Викат Температура размягчения	150	°C	ISO 306/A

Электрический	Номинальное значение	Единица измерения	Метод испытания
Удельное сопротивление поверхности	< 10	ohms	IEC 60093

Инъекция	Номинальное значение	Единица измерения
Температура сушки- Осушитель сушилка	70 - 95	°C
Время сушки- Осушитель сушилка	2.0 - 4.0	hr
Задняя температура	220 - 250	°C
Средняя температура	220 - 250	°C
Передняя температура	230 - 260	°C
Температура сопла	220 - 250	°C
Температура обработки (расплава)	230 - 260	°C
Температура формы	40 - 80	°C

Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.2%. Moisture may lead to smearing and in extreme cases to foaming. Usually the material can be processed over a broad temperature range and can thus be adapted to a wide variety of processing conditions. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Инструкции по впрыску

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing, the moisture content should not exceed 0.2%. Moisture may lead to smearing and in extreme cases to foaming. Usually the material can be processed over a broad temperature range and can thus be adapted to a wide variety of processing conditions. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Тип материала	Категория	Производитель
Pro-fax 7523	PP Impact Copolymer	LyondellBasell Industries
ACCUTECH™ HP0334C40L1	PP Homopolymer	ACLO Compounders Inc.
Borealis PP RC101	PP, Unspecified	Borealis AG
Braskem PP 5E16S	PP Homopolymer	Braskem America Inc.
CP PRYME® Polypropylene PPH100-12M	PP Homopolymer	Chase Plastics Services Inc.
MAJORIS EW886	PP, Unspecified	AD majoris

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

