Описание материалов:
Microthene MP655962 is a rotational molding powder that produces items with very smooth inner surface under a wide range of processing conditions. MP655962 is selected by customers to make a variety of rotomolded items including light globes, storage containers, traffic crash barriers, ducting and equipment housings. This resin exhibits high impact strength at both room temperature and -40°F. It has good warp resistance and stiffness. MP655962 is a UV-stabilized, 35-mesh powder and is also available in pellet form as Petrothene GA655962.
| Главная Информация | |
|---|
| Добавка | |
| Характеристики | - Хорошая ударопрочность
- Хорошая жесткость
- Ударопрочность при низкой температуре
- Устойчивый к деформации
|
| Используется | |
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.945 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 5.0 | g/10 min | ASTM D1238 |
| Экологическое сопротивление растрескиванию (10% Igepal CO-630, F50) | 30.0 | hr | ASTM D1693A |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение 1(Yield) | 22.8 | MPa | ASTM D638 |
| Флекторный модуль | | | ASTM D790 |
| 1% Secant | 993 | MPa | |
| 2% Secant | 841 | MPa | |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| ARM Impact | | | |
| -40°C, 3.18 mm | 47.5 | J | |
| -40°C, 6.35 mm | 183 | J | |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | ASTM D648 |
| 0.45 MPa, Unannealed | 66.0 | °C | |
| 1.8 MPa, Unannealed | 42.0 | °C | |