Polylink Power Cable PP 409/401 (S)
Описание материалов:
A silane grafted Crosslinkable polyethylene compound, curable by exposure to moisture, for insulation of power cables and possessing excellent extrudability at high output rate.
PP 409 has been specially developed for cables up to 72 KV. The special formulation and compounding techniques used ensures that the contamination level is kept within the required limits for this voltage grade.
PP 409 has general melt index range of 0.7 - 1.0 which provides firm stability during extrusion, especially for the thick insulations required for high voltage.
DESCRIPTION :
This compound utilizes the system for crosslinking of polyethylenes developed by DOW coming and known as sioplas. It is a two-component system comprising a silylated ethylene polymer known as the graft copolymer PP 409, and a masterbatch PP401 containing a crosslinking catalyst. The two materials normally used in the ratio of 95 parts graft to 5 parts catalyst masterbatch.
| Главная Информация | |
|---|
| Характеристики | - Crosslinkable
- Хорошая стабильность обработки
|
| Используется | - Кабельная оболочка
- Высоковольтная изоляция
- Изоляция среднего напряжения
|
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.925 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 0.75 | g/10 min | ASTM D1238 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tensile Stress (Break) | 14.5 | MPa | IEC 60811 |
| Растяжимое напряжение (Break) | 400 | % | IEC 60811 |
| Старение | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Изменение прочности на растяжение в воздухе (135°C, 168 hr) | 15 | % | IEC 60811 |
| Изменение растяжения при разрыве воздуха (135°C, 168 hr) | 10 | % | IEC 60811 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Термокомплект 1 | | | IEC 60811 |
| Elongation Under Load
: 200°C | 100 | % | IEC 60811 |
| Permanent Elongation after Cooling
: 200°C | 5.0 | % | IEC 60811 |
| Электрический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Коэффициент мощности (23 °C) 2 | 4.00E-4 | | IEC 250 |
| Сопротивление громкости (20°C) | 1.4E+17 | ohms·cm | IEC 60502 |
| Диэлектрическая прочность | 25 | kV/mm | IEC 60243-1 |
| Диэлектрическая постоянная | 2.20 | | IEC 60250 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Зона цилиндра 1 темп. | 150 | °C | |
| Зона цилиндра 2 температура. | 160 | °C | |
| Зона цилиндра 3 темп. | 170 | °C | |
| Зона цилиндра 4 темп. | 180 | °C | |
| Температура адаптера | 190 | °C | |
| Температура матрицы | 190 | °C | |
| Инструкции по экструзии |
|---|
| Screw water temperature : 60 to70°CScreens : 30,100,30(mesh apertures per linear inch)L/D Ratio: 20Compression: 2.5:1 |
| Примечание |
|---|
| 1 . | 15 min, 0.2 N/mm² |
| 2 . | 50 Hz |