Описание материалов:
Eastar™ EN001 Copolyester is a thermoplastic polyester copolymer. Eastar™ EN001 Copolyester has a relatively slow crystallization rate. This broadens the operating window for extrusion and forming processes and helps maintain good clarity when processing much thicker sheet. Eastar™ EN001 copolyester can also be used for injection molding applications. It is the preferred general-purpose crystallizable PET for thermoforming.
This product has been GREENGUARD INDOOR AIR QUALITY CERTIFIED®.
The GREENGUARD INDOOR AIR QUALITY CERTIFIED® Mark is a registered certification mark used under license through the GREENGUARD Environmental Institute (GEI). GEI is an industry-independent, non-profit organization that oversees the GREENGUARD Certification Program. The GREENGUARD Certification Program is an industry independent, third-party testing program for low-emitting products and materials for indoor environments. For more information about GEI and to obtain printable certificates for Eastman™ Copolyesters, visit www.greenguard.org. Choose Eastman Chemical Company under the Manufacturer category and click search to display a list of our products.
| Главная Информация | |
|---|
| Характеристики | - Сополимер
- Приемлемый пищевой контакт
- Средняя четкость
|
| Используется | - Пищевая упаковка
- Товары для дома
- Спортивные товары
- Игрушки
- Инструменты для письма
|
| Рейтинг агентства | - Управление по санитарному надзору за качеством пищевых продуктов и медикаментов 21 CFR 177,1315
|
| Формы | |
| Метод обработки | - Экструзия
- Литье под давлением
- Экструзионный лист
- Термоформовка
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | | | |
| -- | 1.33 | g/cm³ | ASTM D792 |
| 23°C | 1.33 | g/cm³ | ISO 1183/D |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость Роквелла | | | |
| R-Scale, 23°C | 112 | | ASTM D785 |
| R-Scale, 23°C | 114 | | ISO 2039-2 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения (23°C) | 2400 | MPa | ASTM D638, ISO 527-2 |
| Прочность на растяжение | | | |
| Yield, 23°C | 58.0 | MPa | ASTM D638 |
| Yield, 23°C | 57.0 | MPa | ISO 527-2 |
| Break, 23°C | 25.0 | MPa | ASTM D638, ISO 527-2 |
| Удлинение при растяжении (Break, 23°C) | 120 | % | ASTM D638, ISO 527-2 |
| Флекторный модуль | | | |
| 23°C | 2500 | MPa | ASTM D790 |
| 23°C | 2300 | MPa | ISO 178 |
| Флекторный стресс | | | |
| 23°C | 77.0 | MPa | ISO 178 |
| Yield, 23°C | 84.0 | MPa | ASTM D790 |
| Воздействие | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Зубчатый изод Impact | | | |
| -40°C | 27 | J/m | ASTM D256 |
| 23°C | 40 | J/m | ASTM D256 |
| -40°C | 3.1 | kJ/m² | ISO 180/1A |
| 23°C | 4.5 | kJ/m² | ISO 180/1A |
| Незубчатый изод Impact | | | |
| -40°C | No Break | | ASTM D4218 |
| -30°C | No Break | | ASTM D4218 |
| -20°C | No Break | | ASTM D4218, ISO 180/1U |
| 23°C | No Break | | ASTM D4218, ISO 180/1U |
| -40°C | 170 | kJ/m² | ISO 180/1U |
| -30°C 1 | 190 | kJ/m² | ISO 180/1U |
| Ударное устройство для дротиков | | | |
| -40°C, 2.50 mm, Energy at Peak Load | 1.60 | J | ASTM D3763 |
| -40°C, 3.20 mm, Energy at Peak Load | 2.10 | J | ASTM D3763 |
| 23°C, 2.50 mm, Energy at Peak Load | 26.0 | J | ASTM D3763 |
| 23°C, 3.20 mm, Energy at Peak Load | 31.0 | J | ASTM D3763 |
| -40°C, 2.50 mm, Energy to Peak Force | 0.800 | J | ISO 6603-2 |
| -40°C, 3.20 mm, Energy to Peak Force | 1.00 | J | ISO 6603-2 |
| 23°C, 2.50 mm, Energy to Peak Force | 15.0 | J | ISO 6603-2 |
| 23°C, 3.20 mm, Energy to Peak Force | 18.0 | J | ISO 6603-2 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура отклонения при нагрузке | | | |
| 0.45 MPa, Unannealed | 69.0 | °C | ASTM D648, ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | °C | ASTM D648, ISO 75-2/A |
| Оптический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Коэффициент пропускания (Total) | 84.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |