Описание материалов:
The filled flexible thermoplastic CPE sheath compound material is ideal for low-voltage power and control cables. Wire and cable manufacturers use the material for thermoplastic extrusion processing without investing in continuous vulcanization (CV) equipment. CPE 30-11 REV 2 is especially suitable for cables with larger diameters. The composite material passed the heat/seismic test. This test requires that the cable can withstand bending and twisting without cracking or compression. Good humidity characteristics, oil characteristics and electrical characteristics. The material can be used as power and control cables for fossil fuel power plants and thermal power plants.
| Главная Информация | |
|---|
| Используется | - Кабельная оболочка
- Применение проводов и кабелей
|
| Формы | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.29 | g/cm³ | ASTM D792 |
| Внешний вид | Particles/cubes | | ASTM D2090 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore D, 10 sec) | 42 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Модуль растяжения 1 | 8.27 | MPa | ASTM D638 |
| Прочность на растяжение 2(Break) | 11.7 | MPa | ASTM D638 |
| Удлинение при растяжении 3(Break) | 350 | % | ASTM D638 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Температура ломкости | -35.0 | °C | ASTM D746 |
| Воспламеняемость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Индекс кислорода (1.91 mm) | 30 | % | ASTM D2863 |
| Дополнительная информация |
|---|
| 注释：推荐的预干燥为在175°-185°F环境下4小时。注释：根据螺旋设计不同，典型加工温度处于320° - 390°F之间。请联系技术服务部，获取特定设备的推荐。注释：模制厚板的典型属性（0.075"）；不能视为技术规格。 |
| Примечание |
|---|
| 1 . | Type 4, 510mm/min |
| 2 . | Type 4, 510mm/min |
| 3 . | Type 4, 510mm/min |