LUVOCOM® 1301/CF/20

Категория PPS, Polyphenylene Sulfide
Производитель LEHVOSS Group
Торговая марка LUVOCOM®
Порт Китай Шанхайский порт
Торговые условия FOB, CFR, CIF
Платежное средство L/C, T/T, Western Union
PDF cUgbGU_LUVOCOM1301CF20.pdf
Контактная информация
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Описание материалов:
LUVOCOM®1301/CF/20 is a polyphenylene sulfide (PPS) material, and the filler is 20% carbon fiber reinforced material. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific,.

LUVOCOM®The main features of 1301/CF/20 are:
  • flame retardant/rated flame
  • Conductivity
  • Flame Retardant
  • High stiffness
  • high strength

Typical application areas include:
  • textile/fiber
  • engineering/industrial accessories
  • Automotive Industry
  • business/office supplies
  • medical/health care
Главная Информация
Наполнитель/армирование
  • Армированный углеродным волокном материал, 20% наполнитель по весу
Характеристики
  • Проводящий
  • Жесткий, высокий
  • Высокая прочность
  • Статическая проводимость
  • Хорошее сопротивление ползучести
  • Теплостойкость, высокая
  • Огнестойкий
Используется
  • Текстильные изделия
  • Инженерные аксессуары
  • Применение в автомобильной области
  • Бизнес-оборудование
  • Медицинские принадлежности/принадлежности для ухода
Внешний вид
  • Натуральный цвет
ФизическийНоминальное значениеЕдиница измеренияМетод испытания
Плотность 1.41g/cm³ISO 1183
Формовочная усадка 0.10 - 0.30%DIN 16901
Поглощение воды (23°C, 24 hr)< 0.050%
МеханическиеНоминальное значениеЕдиница измеренияМетод испытания
Модуль растяжения 17000MPaISO 527-2
Tensile Stress (Break)180MPaISO 527-2
Растяжимое напряжение (Yield)1.5%ISO 527-2
Флекторный модуль 16000MPaISO 178
Флекторный стресс 250MPaISO 178
Flexural Strain at Flexural Strength 2.0%ISO 178
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Максимальная рабочая температура- Короткий срок 240°C
ЭлектрическийНоминальное значениеЕдиница измеренияМетод испытания
Insulation Resistance ohmsIEC 60167
ВоздействиеНоминальное значениеЕдиница измеренияМетод испытания
Charpy Unnotched Impact Strength (23°C)18kJ/m²ISO 179/1fU
ТепловойНоминальное значениеЕдиница измеренияМетод испытания
Heat Deflection Temperature (1.8 MPa, Unannealed)260°CISO 75-2/A
Температура непрерывного использования 220°CUL 746B
Викат Температура размягчения 255°CISO 306/A
CLTE- Поток 1.4E-5cm/cm/°CDIN 53752
Теплопроводность 11.1W/m/K
ЭлектрическийНоминальное значениеЕдиница измеренияМетод испытания
Удельное сопротивление поверхности < 1.0E+3ohmsIEC 60093
ВоспламеняемостьНоминальное значениеЕдиница измеренияМетод испытания
Огнестойкость 2V-0UL 94
ИнъекцияНоминальное значениеЕдиница измерения
Температура сушки
    Hot air dryer 100 - 140°C
    Hot air dryer, B 50 - 90°C
Время сушки
    Hot air dryer 2.0 - 4.0hr
    Hot air dryer, B > 4.0hr
Задняя температура 300 - 320°C
Средняя температура 310 - 330°C
Передняя температура 320 - 340°C
Температура сопла 320 - 340°C
Температура обработки (расплава) 330°C
Температура формы 150 - 180°C
Инструкции по впрыску
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information The material does not necessarily have to be predried; when originally sealed containers are used, this process may normally be omitted. Processing temperatures above 360°C may very rapidly cause thermal damage and should therefore be avoided. Post-crystallization may lead to warpage at elevated operating temperatures. This can be counteracted by suitable heat treatment. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. High-temperature polymers place increased demands on the tool steels employed. Please contact us for further information.
Примечание
1 .Hot-Disk, 60x60x3 mm
2 .Not recognized by UL.
Тип материала Категория Производитель
DIC.PPS CZL-5000 PPS DIC Corporation
OnForce™ LFT SF-40LCF/000 Black PPS PolyOne Corporation
RTP 1383 TFE 10 PPS RTP Company
RTP 1387 SI PPS RTP Company
LNP™ STAT-KON™ OE002 compound PPS, Linear SABIC Innovative Plastics
RTP 1387 TFE 13 SI 2 PPS RTP Company
Получите информацию об этом продукте следующим способом.
Телефон+086 13424755533
EMAIL US sales@su-jiao.com

Служба поддержки клиентов Вичат
Copyright © russianpolymer.com All Rights Reserved
Получите информацию об этом продукте следующим способом.
+08613424755533
sales@su-jiao.com

Служба поддержки клиентов Вичат
Свяжитесь с нами