Capran® 1500M

Категория	PA6, Polyamide 6 , Nylon 6
Производитель	Honeywell
Торговая марка	Capran®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	cKnAVt_Capran-1500M.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

CAPRAN® 1500M is a 0.59 mil (15 micron) biaxially oriented nylon 6 film with a polymeric coating which provides enhanced adhesion to a variety of inks, coatings, and adhesives. Metallization adhesion is excellent when using "M" coated products.

Главная Информация
Характеристики	Хорошая адгезия
Используется	Двухосно-ориентированная пленка
Формы	Пленка

Механические	Номинальное значение	Метод испытания
Коэффициент трения		ASTM D1894
With Metal-Dynamic	0.23	ASTM D1894
With self-dynamics	0.75	ASTM D1894

Пленки	Номинальное значение	Единица измерения	Метод испытания
Сектантный модуль			ASTM D882
MD : 15 µm	2760	MPa	ASTM D882
TD : 12 µm	2760	MPa	ASTM D882
Прочность на растяжение			ASTM D882
MD : Break, 12 µm	255	MPa	ASTM D882
TD : Break, 12 µm	255	MPa	ASTM D882
Удлинение при растяжении			ASTM D882
MD : Break, 12 µm	80	%	ASTM D882
TD : Break, 12 µm	80	%	ASTM D882
Проницаемость кислорода (25°C, 12 µm)	1.4	cm³·mm/m²/atm/24 hr	ASTM D3985
Скорость передачи водяного пара (15 µm, 38°C, 100% RH)	330	g·mm/m²/atm/24 hr	ASTM F1249

Оптический	Номинальное значение	Единица измерения	Метод испытания
Блеск (20°)	160 - 175		ASTM D2457
Haze (11.9 µm)	2.2 - 3.3	%	ASTM D1003

Дополнительная информация
Yield: 40800 in²/lbTensile Strength @ Break, ASTM D 882, MD & TD: 34000 to 42000 psiElongation @ Break, ASTM 882, MD & TD: 70 to 90%Secant Modulus, ASTM D 882, MD & TD: 350000 to 450000 psiGraves Tear (initial), ASTM D1004, MD & TD: 1100 to 1500 g/milCoefficient of Friction, ASTM D 1894: 0.60 to 0.90 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.18 to 0.27 vs Metal-DynamicOxygen Permeability, ASTM D 3985: 3.0 to 4.0 cc/100 in²/dayWater Vapor Transmission, ASTM F 1249: 20 to 23 g/100 in²/daySurface Tension, ASTM 2578, minimum, treated side: >/= 56 dynes/cmSurface Tension, ASTM 2578, Minimum, untreated side: >/= 50 dynes/cmDimensional Stability, ASTM D1204, 320°F, 5 mins, MD: 1.5 to 2.5% shrinkageDimensional Stability, ASTM D1204, 320°F, 5 mins, TD: 0.2 to 0.7% shrinkage

Дополнительная информация

Yield: 40800 in²/lbTensile Strength @ Break, ASTM D 882, MD & TD: 34000 to 42000 psiElongation @ Break, ASTM 882, MD & TD: 70 to 90%Secant Modulus, ASTM D 882, MD & TD: 350000 to 450000 psiGraves Tear (initial), ASTM D1004, MD & TD: 1100 to 1500 g/milCoefficient of Friction, ASTM D 1894: 0.60 to 0.90 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.18 to 0.27 vs Metal-DynamicOxygen Permeability, ASTM D 3985: 3.0 to 4.0 cc/100 in²/dayWater Vapor Transmission, ASTM F 1249: 20 to 23 g/100 in²/daySurface Tension, ASTM 2578, minimum, treated side: >/= 56 dynes/cmSurface Tension, ASTM 2578, Minimum, untreated side: >/= 50 dynes/cmDimensional Stability, ASTM D1204, 320°F, 5 mins, MD: 1.5 to 2.5% shrinkageDimensional Stability, ASTM D1204, 320°F, 5 mins, TD: 0.2 to 0.7% shrinkage

Тип материала	Категория	Производитель
Radilon® S LRV300ER 339 E NER	Nylon 6	Radici Plastics
SLOVAMID® 6 GF 50	Nylon 6	Plastcom
Akulon® K224-G6	Nylon 6	DSM Engineering Plastics
ALTECH® PA6 A 4030/100 MR30	Nylon 6	ALBIS PLASTIC GmbH
EMLON® 6 FR V0	Nylon 6	EMAS Plastik San.Tic.AS.
HiFill® PA6 L LE MB	Nylon 6	Techmer Engineered Solutions