Описание материалов:
Quadraflex™ ALE-85A-B20 is high performance aliphatic polyether thermoplastic polyurethane. The polymer is loaded with 20% barium sulfate by weight, is naturally white and supplied in small pellets for ease of processing. The material exhibits excellent mechanical properties, oxidative stability, biocompatibility, elasticity, non-yellowing during aging and softening at body temperature. The resin has consistent melt flow properties making it ideal for extrusion.
Quadrathane™, Quadraflex™, Quadraban™ and Quadraplast™ performance polymers are primarily used in life science and medical applications including vascular access devices, surgical supplies, respiratory devices, tracheotomy devices, and other medical applications. Typical end products include tubing, catheter parts, balloons, and various medical device components. These performance polymers are available in a variety of durometers, radiopacifiers, colors, and custom formulations.
| Главная Информация | |
|---|
| Наполнитель/армирование | - Сульфат бария, 20% наполнитель по весу
|
| Характеристики | - Высокая эластичность
- Антиоксидант
- Обрабатываемость, хорошая
- Хорошая мобильность
- Хорошая стабильность цвета
- Биологическая Совместимость
- Алифатический
- Сопротивление
|
| Используется | - Фитинги для труб
- Хирургические инструменты
- Медицинские принадлежности/принадлежности для ухода
|
| Внешний вид | |
| Формы | |
| Метод обработки | - Экструзия
- Литье под давлением
|
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 1.24 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 7.5 | g/10 min | ASTM D1238 |
| Формовочная усадка-
Поток | 0.60 - 1.0 | % | ASTM D955 |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore A) | 85 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Флекторный модуль | 15.2 | MPa | ASTM D790 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Растяжимое напряжение (10% напряжение) | 4.83 | MPa | ASTM D412 |
| Tensile Stress | | | ASTM D412 |
| 100% strain | 7.58 | MPa | ASTM D412 |
| 300% strain | 15.2 | MPa | ASTM D412 |
| Прочность на растяжение (Break) | 35.9 | MPa | ASTM D412 |
| Удлинение при растяжении (Break) | 500 | % | ASTM D412 |
| Термокомплект | Номинальное значение | Единица измерения | |
|---|
| Время доставки (38°C) | 6.0 - 10 | hr | |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 54.4 | °C | |
| Время сушки | 4.0 | hr | |
| Рекомендуемая максимальная влажность | < 3.0E-3 | % | |
| Задняя температура | 177 | °C | |
| Передняя температура | 191 | °C | |
| Температура сопла | 196 | °C | |
| Температура обработки (расплава) | 204 | °C | |
| Температура формы | 4.44 - 32.2 | °C | |
| Скорость впрыска | Slow | | |
| Коэффициент сжатия винта | 2.5:1.0 - 3.5:1.0 | | |
| Инструкции по впрыску |
|---|
| Injection Speed: 10 g/secCooling/Hold TIme: Long, at least 50% of cycle (20 to 60 secs depending on thickness) |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Температура сушки | 54.4 | °C | |
| Время сушки | 4.0 | hr | |
| Рекомендуемая максимальная влажность | < 0.030 | % | |
| Зона цилиндра 1 темп. | 171 | °C | |
| Зона цилиндра 2 температура. | 182 | °C | |
| Зона цилиндра 3 темп. | 188 | °C | |
| Зона цилиндра 4 темп. | 193 | °C | |
| Температура расплава | 193 | °C | |
| Температура матрицы | 193 - 216 | °C | |
| Back Pressure | 6.89 - 12.4 | MPa | |
| Инструкции по экструзии |
|---|
| Screen Pack: 250 meshScrew Speed: Low sheer, 150 to 250 rpmWater Bath: 80 to 110°F |