Capran® 2500M

Категория	PA6, Polyamide 6 , Nylon 6
Производитель	Honeywell
Торговая марка	Capran®
Порт	Китай Шанхайский порт
Торговые условия	FOB, CFR, CIF
Платежное средство	L/C, T/T, Western Union
PDF	bZ06cM_Capran-2500M.pdf
Контактная информация	EMAIL US  sales@su-jiao.com Служба поддержки клиентов Вичат

Описание материалов:

CAPRAN® 2500M is a 1.00 mil (25 micron) biaxially oriented nylon 6 film with a polymeric coating which provides enhanced adhesion to a variety of inks, coatings, and adhesives. Metallization adhesion is excellent when using "M" coated products.

Главная Информация
Характеристики	Хорошая адгезия
Используется	Двухосно-ориентированная пленка
Формы	Пленка

Механические	Номинальное значение	Метод испытания
Коэффициент трения		ASTM D1894
With Metal-Dynamic	0.23	ASTM D1894
With self-dynamics	0.75	ASTM D1894

Пленки	Номинальное значение	Единица измерения	Метод испытания
Толщина пленки протестирована	25	µm
Сектантный модуль			ASTM D882
MD : 25 µm	2760	MPa	ASTM D882
TD : 25 µm	2760	MPa	ASTM D882
Прочность на растяжение			ASTM D882
MD : Break, 25 µm	255	MPa	ASTM D882
TD : Break, 25 µm	255	MPa	ASTM D882
Удлинение при растяжении			ASTM D882
MD : Break, 25 µm	80	%	ASTM D882
TD : Break, 25 µm	80	%	ASTM D882
Проницаемость кислорода (25°C)	0.71	cm³·mm/m²/atm/24 hr	ASTM D3985
Скорость передачи водяного пара (25 µm, 38°C, 100% RH)	190	g·mm/m²/atm/24 hr	ASTM F1249

Оптический	Номинальное значение	Единица измерения	Метод испытания
Блеск (20°, 25.4 µm)	90 - 140		ASTM D2457
Haze (25.4 µm)	2.3 - 3.4	%	ASTM D1003

Дополнительная информация
Yield: 24000 in²/lbTensile Strength @ Break, ASTM D 882, MD & TD: 34000 to 42000 psiElongation @ Break, ASTM 882, MD & TD: 70 to 90%Secant Modulus, ASTM D 882, MD & TD: 350000 to 450000 psiGraves Tear (initial), ASTM D1004, MD & TD: 1100 to 1500 g/milDimensional Stability, ASTM D1204, 320°F, 5 mins, MD: 1.5 to 2.5% shrinkageDimensional Stability, ASTM D1204, 320°F, 5 mins, TD: 0.2 to 0.7% shrinkageCoefficient of Friction, ASTM D 1894: 0.60 to 0.90 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.18 to 0.27 vs Metal-DynamicOxygen Permeability, ASTM D 3985: 1.3 to 2.3 cc/100 in²/dayWater Vapor Transmission, ASTM F 1249: 11 to 13 g/100 in²/daySurface Tension, ASTM 2578, minimum, treated side: >/= 56 dynes/cmSurface Tension, ASTM 2578, Minimum, untreated side: >/= 50 dynes/cm

Дополнительная информация

Yield: 24000 in²/lbTensile Strength @ Break, ASTM D 882, MD & TD: 34000 to 42000 psiElongation @ Break, ASTM 882, MD & TD: 70 to 90%Secant Modulus, ASTM D 882, MD & TD: 350000 to 450000 psiGraves Tear (initial), ASTM D1004, MD & TD: 1100 to 1500 g/milDimensional Stability, ASTM D1204, 320°F, 5 mins, MD: 1.5 to 2.5% shrinkageDimensional Stability, ASTM D1204, 320°F, 5 mins, TD: 0.2 to 0.7% shrinkageCoefficient of Friction, ASTM D 1894: 0.60 to 0.90 vs Itself-DynamicCoefficient of Friction, ASTM D 1894: 0.18 to 0.27 vs Metal-DynamicOxygen Permeability, ASTM D 3985: 1.3 to 2.3 cc/100 in²/dayWater Vapor Transmission, ASTM F 1249: 11 to 13 g/100 in²/daySurface Tension, ASTM 2578, minimum, treated side: >/= 56 dynes/cmSurface Tension, ASTM 2578, Minimum, untreated side: >/= 50 dynes/cm

Тип материала	Категория	Производитель
VENYL SN007 - 8139	Nylon 6	AD majoris
Titalon® 1400GF	Nylon 6	Titan Plastics Compounds Co., Ltd.
Niretan B 30 N	Nylon 6	Soredi S.p.a.
Durethan® B 40 FAM 000000	Nylon 6	LANXESS Corporation
Petlon R-Prime B2-G25-00-BK	Nylon 6	Petlon Polymers Ltd
Chiao Fu PA6 MC312STG30 BK	Nylon 6	Chiao Fu Enterprises Co., Ltd.

Получите информацию об этом продукте следующим способом.

Телефон	+086 13424755533
EMAIL US	sales@su-jiao.com
Служба поддержки клиентов Вичат

