Описание материалов:
The 500S series is very favourable when transparency and good scratch resistance are required, as well as when there are high surface finish requirements. Unfilled grades have excellent flow and mechanical properties, such as elongation, compression set, tensile and tear strength.
The low density entails lower weight compared to the 600S and 660S series. Unfilled compounds are available in hardness from 0 Shore A to 55 Shore D in translucent and black colours but they can easily be coloured in any shade.
| Главная Информация | |
|---|
| Характеристики | - Bondability
- Приемлемый пищевой контакт
- Хорошая химическая стойкость
- Хорошая устойчивость к погоде
- Устойчивость к царапинам
|
| Внешний вид | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Удельный вес | 0.890 | g/cm³ | ASTM D792 |
| Массовый расход расплава (MFR) (190°C/2.16 kg) | 1.0 | g/10 min | ASTM D1238 |
| Формовочная усадка | 0.80 to 2.0 | % | |
| Твердость | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Твердость дюрометра (Shore A) | 55 | | ASTM D2240 |
| Механические | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение | | | ASTM D638 |
| -- | 6.00 | MPa | |
| 100% Strain | 2.00 | MPa | |
| 300% Strain | 3.00 | MPa | |
| Удлинение при растяжении (Break) | > 600 | % | ASTM D638 |
| Эластомеры | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Tear Strength | 24.0 | kN/m | ASTM D624 |
| Комплект сжатия (23°C, 72 hr) | 20 | % | ASTM D395 |
| Тепловой | Номинальное значение | Единица измерения | |
|---|
| Service Temperature | -50 to 125 | °C | |
| Инъекция | Номинальное значение | Единица измерения | |
|---|
| Температура обработки (расплава) | 180 to 210 | °C | |