Описание материалов:
Indothene-HD grade 50GF003 is a blown film grade of High Molecular Weight High Density Polyethylene (HM-HDPE), produced by Hostalen Stirred Tank Heavy Diluent (STHD) Slurry process at Gandhar. It possesses bimodal molecular weight distribution, which improves processability. 50GF003 can readily be processed on HMHDPE blown film extrusion lines. The films will have homogeneous, finely textured, opaque appearance and exhibit very good mechanical properties.
FOOD CONTACT APPLICATIONS :
This grade meets the requirements of Indian Standard IS-10146-1982 on "Polyethylene for its safe use in contact with food stuffs, pharmaceuticals and drinking water". It also conforms to the positive list of constituents as approved in IS:10141:1982. The grade complies with FDA regulation : CFR title 21 , 177.1520, Olefin polymer
| Главная Информация | |
|---|
| Характеристики | - Высокая Молекулярная масса
- Соответствие пищевого контакта
|
| Используется | |
| Рейтинг агентства | - Управление по санитарному надзору за качеством пищевых продуктов и медикаментов 21 CFR 177,1520
|
| Внешний вид | |
| Формы | |
| Метод обработки | |
| Физический | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Плотность | 0.950 | g/cm³ | ASTM D1505 |
| Массовый расход расплава (MFR) | | | ASTM D1238 |
| 190°C/21.6 kg | 8.0 | g/10 min | ASTM D1238 |
| 190°C/5.0 kg | 0.30 | g/10 min | ASTM D1238 |
| Пленки | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Прочность на растяжение | | | ASTM D882 |
| MD
: Yield, 20 µm, blown film | 32.0 | MPa | ASTM D882 |
| TD
: Yield, 20 µm, blown film | 30.0 | MPa | ASTM D882 |
| MD
: Broken, 20 µm, blown film | 56.0 | MPa | ASTM D882 |
| TD
: Broken, 20 µm, blown film | 50.0 | MPa | ASTM D882 |
| Удлинение при растяжении | | | ASTM D882 |
| MD
: Broken, 20 µm, blown film | 550 | % | ASTM D882 |
| TD
: Broken, 20 µm, blown film | 650 | % | ASTM D882 |
| Ударное падение Dart 1(20 µm, Blown Film) | 8.0 | g | ASTM D1709 |
| Elmendorf Tear Strength | | | ASTM D1922 |
| MD
: 20 µm, blown film | 0.50 | g | ASTM D1922 |
| TD
: 20 µm, blown film | 15 | g | ASTM D1922 |
| Тепловой | Номинальное значение | Единица измерения | Метод испытания |
|---|
| Викат Температура размягчения | 125 | °C | ASTM D1525 |
| Экструзия | Номинальное значение | Единица измерения | |
|---|
| Зона цилиндра 1 темп. | 180 | °C | |
| Зона цилиндра 2 температура. | 200 | °C | |
| Зона цилиндра 3 темп. | 210 | °C | |
| Зона цилиндра 4 темп. | 220 | °C | |
| Температура матрицы | 215 | °C | |
| Инструкции по экструзии |
|---|
| Blow up ratio: 3 to 5Neck height: 60D to 8D (D-Die dia) |